控制阀支架的铸造工艺.pdfVIP

学兔兔 控制阀支架的铸造工艺 乐国荣 (福斯流体控制 (苏州)有限公司，江苏 苏州 215021) 摘要：支架是控制阀的关键部件之一。铸件的壁厚悬殊较大，铸造质量要求高，不允许铸件有 较大的铸造缺陷。对控制阀支架铸件的铸造工艺进行了分析和实际试生产验证，确定采用平做 竖浇工艺方案，较好地解决了铸件的疏松缺陷，生产的控制阀支架铸件达到x射线探伤四级以 上的验收标准要求。 关键词：控制阀支架；铸造工艺；球墨铸铁件 中图分类号：TG255 文献标识码：B 文章编号：1 673-3320(201 4)03—0038-03 Casting Process of Control Valve Yoke LE Guorong (Flowserve Fluid Motion and Control(Suzhou)Co．，Ltd．，Suzhou 21 5021，Jiangsu，China) Abstract：Y_oke is one of the key components for con仃ol valve．The castings with bigger wall thickness and high quality requirement are not allowed to appear the larger casting defects．The casting process of control valve yoke castings was analyzed，and the actual production was verified．The process program with horizontally molding and vertically pouring was confirmed to solve the porosity defects of castings preferably．The control valve yoke castings can meet the acceptance requirements of more than four grade with X．ray radiographic inspection． Key words：control valve yoke；casting process；ductile iron casting 控制阀支架是阀门产品的关键部件之一。该 许存在裂纹或疏松等缺陷，故该铸件对铸造工艺 系列铸件材质为球墨铸铁，牌号为ASTM A536 要求相当严格。 60—40—18【 】(相当于QT400—1 8)，其系列铸件质量 最轻的4 kg，最重的345 kg。以单重52 kg的 1 平做平浇工艺方案 01 654控制阀支架铸件为例，其壁厚悬殊较大， 以两圆盘中心和两长方形立柱中心为分型 最小壁厚5 mm，最大壁厚50 mm；铸件上、下为 面，水平造型、水平浇注是最常见的铸造工艺。 大小不一的圆盘 (法兰)，两根长方形立柱将它们 由于是球铁件，为保证铸件内部质量良好，采取 相连，故与圆盘交接处是热节区，铁水凝固时极 了放置冷铁激冷和冒口补缩的工艺方案。 易在该部位形成内部疏松。控制阀支架不同于其 1．1 冷铁位置 他阀门支架，其他阀门支架只是起支撑作用，而 按基本思路冷铁放置在铸件壁厚厚大处。如 控制阀支架还需要连接定位器、电磁阀和过滤减