高耐寒型改性丙烯酸酯防水乳液的合成及应用.pdfVIP

学兔兔 材料研究 ■ 高耐寒型改性丙烯酸酯防水 乳液的合成及应用 毛雄伟，耿立滨，游 洪 (浙江新力化工有限公司，浙江 上虞 312352) 摘要：研制了一种高耐寒型有机硅改性丙烯酸酯乳液，探讨了其合成工艺和性能影响因素。结果表明，采用预乳化半连 续滴加法和后加有机硅单体的方法，可以制得性能稳定的耐寒改性乳液。由该耐寒改性乳液制得的Js防水涂料，各项 性能指标均达到或超过GB／T 23445--2009(聚合物水泥防水涂料》的要求，尤其I型涂料的低温柔性可达一2O 。 关键词：js防水涂料；丙烯酸酯乳液；高耐寒型；有机硅改性 文章编号：1007—497X(2014)一22—0029—04 中图分类号：TU502；TU56 1．65 文献标识码：A Synthesis and Application of Highly Cold-resistant Modified Acrylate Waterproofing Emulsion Mao Xiongwei，Geng Libin，You Hong (Zh~iang Xinli Chemical Co．，Ltd．，Shangyu，Zhejiang 3 12352，China) Abstract：A highly cold—resistant organosilicon modified acrylate emulsion was developed and its synthesis process and performance influence factors were discussed．The results showed that cold—resistant modified emulsion with stable performances could be obtained by pre emulsified semi continuous emulsion and after addition of organosilicon monomer．The performance indexes of js waterproofing coating prepared by the cold—resistant modified emulsion achieved or exceed the requirements of GBFF 23445--2009“Polymer cement waterproofing coating”，and the low temperature inflexibility of I type JS waterproofing coating reached一20℃． · Key words：js waterproofing coating；acrylate emulsion；highly cold—resistant；organosilicon modification 聚合物水泥防水涂料(下称JS防水涂料)是以聚 北方冬季寒冷气候下的应用要求。本课题采用先进 合物乳液(如丙烯酸酯乳液、EVA乳液等)和无机粉 的聚合工艺和特殊的功能单体，制备出了一种高耐寒 料(水泥、石英粉及添加剂等)复合而成的双组分防水 型改性丙烯酸酯防水乳液(下称耐寒改性乳液)，由该 涂料，既有聚合物涂膜的延伸性、防水性，也有水硬性 乳液制得的Js防水涂料即使在低温条件下仍然具有 胶凝材料强度高、易与潮湿基层粘结的优点，因此广 较好的综合性能。本文介绍了该耐寒改性