莱钢1000m^3高炉大煤比烟煤混喷技术应用.pdfVIP

莱钢科技 第5期(总第131期) 莱钢1 000 m3高炉大煤比烟煤混喷技术应用 孙建设 林晓辉 (炼铁厂) 摘 要：高炉在高煤比的前提下进行烟煤混喷，能有效提高煤粉的燃烧率，是炼铁降低成本的有效手 段。莱钢1000 m 高炉通过精料技术和探索合理的操作制度，优化喷煤控制参数，进行烟煤混喷试验 在 烟煤和无烟煤比例达到4：6，煤比维持在180 kg／t，高炉保持了稳产高产。 关键词：高炉 精料 烟煤混喷 含氧量 The Application of the High-coal-ratio Soft Coal Mixed Injection Technique for 1000-Ill Blast Furnace Sun Jianshe Lin Xiaohui (The Ironworks) Abstract：Soft coal mixed injection under the precondition of high coal ratio can effectively enhance pulver— ized coal~combustion rate in blast furnace，as an effective means of reducing cost．Through high grade burden technique and probe into rational operation system，optimizing coal injection control parameters，experimenting on soft coal mixed injections．the 1000 m blast furnace in Laigang maintains steady and high productivity with the ra- ti0 of soft coal and anthracite at 4：6，coal ratio being 180 kg／t． ． Key words：blast furnace；high—grade burden；soft coal mixed injection；oxygen content 1 概述 3 混喷技术措施 莱钢1000 m 高炉采用陶瓷杯炉缸，PW串罐式 根据烟煤的特点，制定了严格喷煤的控制参 无料钟炉顶，全干法煤气除尘系统，卡鲁金顶燃式热 数，以确保混喷安全。高炉制定相应的措施，并对 风炉，软水密闭循环等先进工艺。2007年煤比煤比 喷煤、高炉各控制参数加以调整，使烟煤混喷得以 基本稳定在175 kg／t以上。为了进一步降低生铁成 顺利实施。在高煤比的前提下，烟煤和无烟煤的比 本，1000 m 高炉2007年3月下旬到5月中旬进行 例达到4：6，挥发份16％左右。 烟煤混喷实验，取得了较好效果，在混喷期间，1 3．1 喷煤参数控制 1000 m 高炉煤比达到220 kg／t，平均180 kg／t以上。 混煤制粉条件：确保氧量分析仪参数准确，灵 敏可靠。保证新二区煤场进场原煤按照烟煤比无烟 2 混煤情况 煤3：7的煤量要求均匀存煤。保证氮气压力在0．6 MPa以上，满足喷吹要求。保证事故充氦及其它预 烟煤挥发分高，在 10％ ～40％之间，碳含量为 警参数 (煤粉温度、喷吹压力等)灵活可靠、准 76％～85％，发热量较无烟煤低，热值为2．71～