连续变温下早龄期混凝土应变时变规律试验探究摘 要：针对早龄期混凝土开裂现象，为掌握其应变变化规律，通过日大气温度变化影响下早龄期混凝土应变随时间变化的模拟试验，采集试件的应变及重量数据，分析早龄期混凝土在日气温变化影响下的应变变化规律。研究结果表明：在日气温变化的升温和降温过程中，早龄期（3d内）混凝土均数次出现量级达100×10-6的剧烈收缩，受到约束时可产生易使混凝土开裂的应力；不同水灰比混凝土之间的膨胀应变差值、收缩应变差值分别可达100×10-6、200×10-6。 关键词：混凝土；应变；时变规律；连续变温；早龄期 中图分类号：U444 文献标志码：A 文章编号：1674-4764（2012）02-0058-05 Experimental Analysis of Time-Dependent Law of Early Age Concrete Strain Considering Continuous Temperature Variation QIN Yua，LIU Lai-juna，ZHI Xi-lanb，ZHANG Liu-yua (a. School of Highway; b. Key Laboratory for Special Area Highway Engineering of Ministry of Education, Changan University, Xian 710064, P. R. China) Abstract:Arexperiment was carried out for the analysis of time-varying regularity of early-age concrete strain under the influence of free air temperature changes. The strain data and the weight of specimens were collected. It is found that the severe shrinkage of early age (≤3d) concrete appears in the course of heating and cooling of daily temperature. And the magnitude of the severe shrinkage is 100×10-6. The expansion strain difference is up to 100×10-6 for different water cement ratio concrete, and the shrinkage strain difference is up to 200×10-6. Key words:concrete；strain；time-dependent law；consecutive temperature variation；early age  混凝土桥梁构件早期开裂一直是业内关注的重要问题。受到自身或外界约束时，早龄期混凝土应变（由水化反应、收缩等内因和环境温度、湿度等外因产生）会产生应力，从而导致混凝土开裂，进而影响桥梁结构的耐久性，甚至安全性。现浇混凝土桥梁构件早期开裂现象尤为多见。 早龄期混凝土应变问题已有较多研究成果。Aitcin等提出混凝土自收缩主要发生在初凝至1 d龄期内，之后自收缩增加速率趋于缓慢［1］。Nassif等认为对于非常低的w/c+p，粉煤灰轻集料提高了混凝土自收缩性能［2］。高小建等认为其他配合比参数不变时混凝土早期自收缩与水灰质量比的关系近似成二次方程［3］。张武满和孙伟［4］指出高性能混凝土早期自收缩随测试时间、砂率和针片状骨料含量的增加而增大，随骨料最大粒径的增大而减小。已有研究工作主要集中在混凝土早期收缩的影响因素［1，3-6］、收缩试验研究［7-8］、各种混凝土早龄期收缩特性［9-11］等。但早龄期混凝土在大气温度下应变随时间变化的试验研究尚未见报道。 通过早龄期混凝土应变随温度、时间变化的模拟试验，采集混凝土试件应变及重量变化数据，分析不同配合比混凝土在温度影响下的应变差异，探讨在日气温连续变化影响下早龄期混凝土应变随时间变化的规律。 1 试验方案设计 试验目的：通过中国北方（指淮河、秦岭和昆仑山以北的广大区域［12］）7月份日气温变化模拟环境下的应变试验，得出早龄期混凝土在日气温连续变化影响下的应变时变规律。受气候影响，夏季是中国北方桥梁施工的主要季节。故选取7月作为模拟试验的时间点。 试验流程：