轧后水冷生产轴承钢的实验研究.pdfVIP

材料热处理技术 MaterialHeat Treatment 2OO8年1月 轧后水冷 承钢的实验研究 闫 肃。宋庆功 (中国民航大学 理学院．天津300300) 摘 要：研究了GCrl5轴承钢棒材轧后水冷对所析出的珠光体形态和网状碳化物级别的影响，结果表明：在 其他工艺参数相同的情况下，随着轧后冷却时间的延长，珠光体球团直径和片层间距减小，网状碳化物级别降低， 水冷后返红温度为7l5℃时，可以得到细小的珠光体和少量弥散分布的碳化物，返红温度在7l5℃以下．随着温 度继续降低对组织影响不大。 关键词：轴承钢；快冷工艺；细片状珠光体；刚状碳化物 ’ 中图分类号：TG142．4 文献标识码：A 文章编号：1001．3814(2008)02．0080．02 Experimental Study on Bearing Steel Produced by Water Cooling Technology after Rolling YAN Su，SONG Qinggong (College ofScience，Civil Aviatmn University ofChina,Tianjin 300300，China) Abstract：The influences of accelerated cooling technology after rolling on pearlite and network carbide were studied．Th e experimental results indicate that the diameter of pearlite colony and the distance of lam ellar pearlite decrease with the increase of cooling time，and the grade of network carbide reduces．Fine lamellar Pearlite and a little discontinuous carbide are obtained when the temperature after cooling is 7 1 5℃，the influence on the structure is small when temperature after cooling is below 7 1 5℃． Key words：bearing steel；accelerated cooling technology；fine lam ellar pearlite；network carbide GCr15由于其良好的综合性能而成为轴承行 加热到l l00℃保温l h，出炉后在l 000℃进行3 业中应用最广泛的钢种之一。为了满足用户对 道次轧制，轧后厚度为20 mm。轧后立即进行水 GCrl5轴承钢棒材冷加工性能要求的不断提高， 冷，水冷时间为l~4 s，水冷返红后将钢板放人铺 要求生产厂家采用控轧控冷工艺来控制棒材的显 有石棉毡的铁箱内进行缓冷。将轧后试样沿轧制 微组织即控制奥氏体晶粒以细化珠光体球团，减 方向切开，应用高倍光学金相显微镜对TD面(平 小珠光体片层间距以获得索氏体组织。抑制网状 行于轧制方向且垂直于轧制面)的显微组织进行 碳化物的析出【”，在GCr15连轧生产线上改进轧 观察，金相试样用4％硝酸酒精腐蚀。 后冷却工艺是提高产品组织性能的主要措施。本 为清晰地观察GCrl5变形后的碳化物网．对 文在实验室条件下研究了轧后不同水冷时间对