关于混凝土抗冻性理论研究及其在冬季施工中应用.docVIP

关于混凝土抗冻性理论研究及其在冬季施工中应用摘要：混凝土作为施工项目的主要施工材料，其在建筑施工中的地位越来越被重视。随着科学技术的发展与进步，施工项目基本不受季节因素限制，可严寒地区的部分建筑物仍然发生了冻融破坏现象，严重影响着建筑物的质量和安全，使抗冻性成为考核混凝土质量的重要指标。为此，本文初步分析了混凝土抗冻性理论的相关内容，以及冬季施工的基本要求和措施。 关键词：混凝土；抗冻性；原因；冬季；应用 Abstract: Concrete as a construction project’s main construction material, its position in the construction more and more attention. With scientific and technological development and progress of the construction project basically not subject to seasonal factors limit the cold region some of the buildings are still the freeze-thaw damage, serious impact on the quality and safety of buildings, the assessment of concrete frost resistance an important indicator of quality. In this paper, a preliminary analysis of concrete frost resistance of the content of the theory, as well as winter construction of the basic requirements and measures. Keywords: concrete; frost resistance; reason; winter; application. 中图分类号：TU528文献标识码：A文章编号： 在我国，气候具有显著的区域性特征，严寒地区的许多建筑物或多或少都发生过冻融破坏现象，威胁着建筑物和人们生命财产的安全。因而，抗冻性成为了衡量混凝土施工质量的重要指标，提高混凝土的抗冻性势在必行。及时保障建筑物施工质量的必然要求，也是保证人们生命财产安全的重要基本条件。这种情况下，有必要扼要分析混凝土抗冻性理论及冬季施工的基本要求和措施，全面保证严寒地区建筑物的施工质量。 一、混凝土抗冻性理论相关内容分析 （一）混凝土冻融损伤的基本类型 混凝土冻融损伤基本包括两种情况：一是表面损伤，比如剥落脱皮等；二是内部损伤。从混凝土表面并不能看出内部损伤的特征，但其危害性是极大的，严重时甚至可以改变混凝土性质，比如降低弹性模量等。 （二）混凝土冻融损伤的基本原因 1、新拌混凝土冻融损伤的原因 新搅拌的混凝土由于空隙率高、含水量多、强度低，比较容易发生冻融损伤现象。发生机理为：混凝土表面降温冷却时，冷流向结构内延伸，并在深处空穴中逐渐冻结。一般情况下，由空隙大的空穴开始形成晶状体，逐渐增大的同时蔓延到其他部位，形成宏观移动。晶状体形成、增大过程中倘若混凝土材料不能承受其所带来的拉应力，则导致混凝土结构抗拉强度发生破坏，进而损坏混凝土结构。 2、成熟混凝土冻融损伤的基本原因 成熟混凝土产生冻融损伤主要与两个方面有关：一是内应力，二是静压力。混凝土结构中的孔径分为凝胶孔、毛细孔和气泡孔，可冻水主要集中在水泥石和骨料颗粒的毛细孔中，凝胶孔中的水不可能就地冻结，气泡孔中的水易冻结。通常情况，混凝土结构中孔径的空隙是连续分布的，其中存在的水分按照一定顺序冻结，温度越低，可冻水越多。在某一固定负温下混凝土结构中只存在部分可冻水，当孔径中的实际冻水超过可冻水体积，多余的体积必然对混凝土造成破坏力，导致混凝土结构出现损坏。发生机理为：水化过程中混凝土内部形成凝胶体，连续分布的孔径网络被分割成一个个独立的毛细孔，与周围的凝胶孔构成了渗水器壁。随着水化不断深入，混凝土的致密性和温度逐渐下降，可冻水逐渐增多，渗水器壁的渗水性能下降，最终因疏导不畅、冰晶膨胀增大导致混凝土内部产生内应力和静压力，致使混凝土结构发生破坏。 另外，骨料作为混凝土结构的重要组成部分，倘若其冷冻膨胀也会导致混凝土破裂。因此，为了保证混凝土结构在冬季的完好性，需要确保骨料不遭受到破坏。当骨料颗粒达到一定程度以上，混凝土内部水压力因超过骨料的破裂强度而发生内部结构破坏。因此