氩弧焊（Argon arc welding）.doc

氩弧焊（Argon arc welding） Mainly to protect the gas problems, including: 1, argon is not pure. 2 argon flow is too small. 3, after the torch arc quickly left the weld area before the welding area without argon cooling. 4, the environment is windy, blowing argon. The solution is: 1. When filling argon, we should clean argon gas bottle and fill pure argon gas. 2, adjust the argon pressure reducing valve, ensure output of.3, arc reasonable after remain in place until the end of the jet gun. 4, appropriate shelter, shelter from the wind. Answer: wallowers long | two | 2011-1-14 11:03 1. weld surface oil and dirt, too dirty; 2. argon protection is not good: argon flow is not enough, argon purity is not enough, the pipeline leak, and the welding area air flow is too large; 3. material is not suitable for welding by argon arc welding. What are the arc energy parameters that determine the weld formation? Welding current I, arc voltage U and welding speed Vw are the main energy parameters which determine the formation of welding seam. In production, these three parameters are usually defined as the standard parameters of automatic arc welding. In addition, the diameter of the electrode and wire extension electrode (wire), inclination angle, inclination angle, groove shape and welding plate thickness, electrode type and polarity, protection conditions, base metal and weld components and trace elements have a certain effect on weld forming. What is the effect of welding current on weld formation? When other conditions are constant, the welding current is increased, the weld penetration and the increase are increased, while the weld width remains almost unchanged (or slightly increased). The results are shown in submerged arc welding. This is because: (1) when the welding current is added, the thermal power arc and arc force increases, so the volume and crater depth of the weld pool are not with the current increase, experiments show that the protection on the wire diameter, condi