aging behaviour of al-mg-si alloys subjected to severe plastic deformation by ecap and cold asymmetric rolling老化行为由ecap al-mg-si合金受到严重的塑性变形和冷不对称轧制.pdf

1、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。。
2、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
3、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
4、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
5、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
6、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
7、VIP文档为合作方或网友上传，每下载1次，网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档

aging behaviour of al-mg-si alloys subjected to severe plastic deformation by ecap and cold asymmetric rolling老化行为由ecap al-mg-si合金受到严重的塑性变形和冷不对称轧制

Hindawi Publishing Corporation Journal of Metallurgy Volume 2011, Article ID 959643, 8 pages doi:10.1155/2011/959643 Research Article Aging Behaviour of Al-Mg-Si Alloys Subjected to Severe Plastic Deformation by ECAP and Cold Asymmetric Rolling ` S. Fare, N. Lecis, and M. Vedani Dipartimento di Meccanica, Politecnico di Milano, via Giuseppe La Masa, 1, 20156 Milan, Italy Correspondence should be addressed to M. Vedani, maurizio.vedani@polimi.it Received 22 March 2011; Accepted 12 June 2011 Academic Editor: Enrico Evangelista ` Copyright © 2011 S. Fare et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. A study was carried out on aging behaviour of a 6082 alloy processed by two diﬀerent severe plastic deformation techniques: ECAP and asymmetric rolling. Both techniques were able to generate an ultraﬁne-grained structure in samples processed at room temperature. It was stated that severe straining promotes marked changes in the postdeformation aging kinetics. The peaks of β/β transition phases were anticipated and of progressively reduced intensity over the coarse grained alloy. A further peak accounting for onset of recrystallization also appeared in the most severely deformed samples. Full consistency in peak shape and position was found when comparing materials processed by ECAP and asymmetric rolling. Isothermal aging treatments performed at 180◦C revealed that in the severely deformed samples, aging became so fast that the hardness curves continuously decreased due to overwhelming eﬀects of structure restoration. On the contrary, aging at 130◦C oﬀers goo