硅烷偶联剂对金属托槽及瓷面黏接强度影响.docVIP

硅烷偶联剂对金属托槽及瓷面黏接强度影响 　【摘要】 目的 研究硅烷偶联剂（CP）的使用对金属托槽与瓷面黏接强度的影响。 方法 150个烤瓷试件按不同瓷面处理随机分5组：A组喷砂处理；B组金刚砂车针打磨；C组9.6%氢氟酸酸蚀3 min；D组37%的磷酸酸蚀1 min；E组为未处理组。再根据是否使用CP各分2小组，每小组15个试件。黏接剂为3M UniteTM黏接剂（3M）。托槽粘接后在5 ℃和55 ℃水浴箱之间进行冷热水温度循环实验，使用材料实验机检测抗剪切强度，并记录瓷破裂指数（PFI），计算瓷破损率。 结果 使用CP后平均抗剪切强度有显著提高，与未使用CP组比较差别有统计学意义（Plt;0.05）；瓷破裂率高于未使用CP组，两组比较差别有统计学意义（Plt;0.05）。 结论 瓷面经处理后使用CP粘接托槽可达到满意的粘结强度，但瓷面破损及重新修复的机率增加。 【关键词】 硅烷类； 复合树脂类； 正畸矫正器； 陶瓷金属粘固剂 　　ABSTRACT: Objective To investigate the influence of silane coupling agents ceramic primer（CP）on the bond strength of metal meshbacked brackets to porcelain. Methods 150 glazed porcelain faces were randomly divided into 5 groups according to different conditioning techniques: (A)sandblasting with 50 μm Al2O3 particles, (B)deglazing by grinding, (C)etching with 9.6% hydrofluoric acid(HF) for 3 min, (D)etching with 37% phosphoric acid(H3PO4)for 1 min, (E) untreated. Each group was further divided into 2 experimental groups according the surface treatment with CP or without CP treatment. 3M UniteTM adhesive were utilized to bond the bracket onto each sample. All specimens went through with 5 ℃ and 55 ℃ circled fatigue experiment. The shear bond strength was determined and the results were analyzed. Results The silanating CP groups resulted in a statistically significant higher bond strength. The rates of porcelain fracture in the surface silanating CP groups was higher than that of omission CP groups. Conclusions The use of a silane primer CP after porcelain surface preparation can gave acceptable results for clinical use when metal brackets bond porcelain, but the silane primer application was associated with increased porcelain surface damage. 　　KEY WORDS: silanes; composite resins; orthodontic appliances; cermet cements 　　黏接托槽是正畸临床应用固定矫治器的重要步骤之一，黏接强度与矫治效果密切相关。随着烤瓷修复体在临床上的广泛应用，以及成年正畸患者的增加，如何简单方便地在瓷面上粘接托槽，获得满意的黏接强度，是广大正畸医生关心的问题。硅烷偶联剂(ceramic primer,CP)是一种有效的瓷表面处理剂，已被广泛地应用于处理硅酸盐系全瓷材料的粘接面，以增强其与树脂黏接剂的结合强度。本研究探讨瓷面经喷砂、机械打磨、酸蚀刻等不同方法处理后，使用CP对托槽与瓷面黏接强度的影响。