60Si2Mn弹簧钢热处理工艺及组织性能研究.doc

60Si2Mn弹簧钢热处理工艺及组织性能研究 摘要:通过对同60Si2Mn弹簧钢进行不同的热处理，测定强度、硬度、塑韧性的变化情况，对比真空条件和普通条件下热处理结果分析我们可以得到，真空条件下的热处理可以有效的改善硅锰钢容易脱碳的缺陷，真空球化热处理后，材料的硬度比普通热处理高。不同条件下进行热处理的结果表明：对60Si2Mn弹簧钢进行球化退火+870℃淬火（油淬）关键词：eat treatment process and structure property research of 60Si2Mn spring steel Abstract：60Si2Mn spring steel with different heat treatments and test the change of strength 、 hardness 、?plasticity and toughness . we can get the result that the heat trement under acuum conditiovn can defects decarburization of silicon manganese steel comparing to acuum conditiovn and normal condition heat treatment . material’s hardness is higher than the ordinary heat treatment after spheroidizing under vacuum heat treatment. the results of different heat treatments show that the 60Si2Mn spring steel’s comprehensive mechanical property is the best with spheroidizing annealing ，quenching under 870℃ in oil and tempering under 350℃. Under. It is a kind of ideal heat treatment process in ?present conditions . Keywords: 60Si2Mn spring steel , Heat treatment , Mechanical?property 目录 1 绪论 1 1.1 研究60Si2Mn弹簧钢的目的和意义 1 1.2 60Si2Mn弹簧钢国内外研究进展 1 1.3 60Si2Mn弹簧钢热处理研究的内容 2 1.3.1 弹簧钢的定义 2 1.3.2 弹簧的服役条件 3 1.3.3 常见弹簧钢的化学成分特点 3 1.3.4 常见弹簧钢的分类 4 2 热处理过程 6 2.1 热处理 6 2.1.1 热处理的定义 6 2.1.2 热处理的作用 6 2.1.3 热处理的条件 7 2.1.4 弹簧钢的热处理方法 7 2.2 常用热处理工艺的概念及目的 8 2.2.1 退火 8 2.2.2 正火 8 2.2.3 淬火 9 2.2.4 回火 9 2.3 热处理工艺的制定 9 2.3.1 热处理过程 12 2.4 热处理前后显微组织观察 15 2.4.1 金相试样的制备 15 2.4.2 各热处理条件下的金相组织 17 2.5 热处理后的力学性能 24 2.5.1 硬度的测定 24 2.5.2 冲击韧性的测定 25 2.5.3拉伸实验 26 3 实验结果与分析 28 3.1热处理实验结果 28 3.2 热处理实验结果的分析 30 4 结论 31 参考文献 31 致 谢 32 1 绪论 1.1 研究60Si2Mn弹簧钢的目的和意义 新中国成立以来，我国在各个方面取得了重大突破，一九七八年拉开的改革序幕，将我国与世界紧密的联系在了一起。随着改革的深入，我国在政治、文化经济等各领域取得了举世瞩目的成绩，尤其是我国的经济，经过三十多年的发展，人们的生活水平得到显著地提高，汽车成为了人们生活中必不可少的交通工具，我国是汽车产销大国，弹簧作为汽车的零部件具有非常重要的作用。弹簧的用途非常广泛，是工业生产中 必不可少的机械零件，无论是飞机、火车等庞然大物，还是非常精密的仪表都离不开它，当受到外力冲击时，弹簧发生形变吸收能量达到缓冲的目的，这就要求做弹簧的材料具有高的弹性极限。实际工作过程中弹簧一般要经受反复的冲击，是在交变应力条件下工作的，这样的工作条件就决定了弹簧必须具有高的疲劳极限和抗拉强度。 生活当中，我们有多种形式的弹簧，最常见的