3MZ350纳米复合树脂、3M自酸蚀粘结剂联合.docVIP

精品论文 参考文献 3MZ350纳米复合树脂、3M自酸蚀粘结剂联合 张春芝 　　（吉林省吉林油田总医院口腔科吉林吉林138000） 　　【摘要】目的：评价3MZ350纳米复合树脂、3M自酸蚀粘结剂联合排龈术修复牙颈部楔状缺损的临床疗效。方法：60例150颗牙采用3MZ350纳米复合树脂、3M自酸蚀粘结剂联合排龈术修复牙颈部楔状缺损。治疗后6个月、2年复查，以改良的美国公共健康部（USPHS）制定的评定系统标准记录修复效果。结果：治疗后6个月修复体固位率为100%，无脱落及继发龋，治疗后2年修复体固位率为98%，有2颗边缘着色，1颗修复体部分脱落。结论：3MZ350纳米复合树脂、3M自酸蚀粘结剂联合排龈术修复牙颈部楔状缺损的临床疗效肯定，是修复牙颈部楔状缺损较理想的一种方法。 　　【关键词】纳米复合树脂；自酸蚀粘结剂；排龈术；楔状缺损Clinical efficacy of 3M Z350 nano-composite resin,3M self-etching adhesive joint retraction of wedge-shaped defect 　　Zhang Chunzhi(Department of Stomatology,General Hospital of Jinlin Oil Field of Jilin province 138000) 　　【Abstract】Objective:To evaluate the clinical effects of 3M Z350 nano-composite resin,3M self-etching adhesive joint retraction of wedge-shaped defect.Methods:60 cases of 150 teeth with 3M Z350 composite resin,3M self-etching adhesive joint retraction of wedge-shaped defect.Review 6 months after treatment,2 years,the United States of America to improve the Department of public health (USPHS) to develop the assessment system of standard recording restoration effect.Results:After the treatment,6 months prosthesis retention rate was 100%,no shedding and secondary caries,2 year after treatment prosthesis retention rate was 98%,with 2 edge coloring,1 restorations part off.Conclusion:The clinical efficacy of 3M Z350 nano-composite resin,3M self-etching adhesive joint retraction of wedge-shaped defect,is an ideal method of wedge-shaped defect. 　　【中图分类号】R453【文献标识码】B【文章编号】1003-5028(2013)10-0109-02 　　牙颈部楔状缺损是牙齿硬组织在某种因素长期作用下缓慢丧失，形成由两个光滑斜面组成的楔形缺损。表浅的缺损无任何症状，缺损深达牙本质后可出现牙本质过敏症，深达牙髓时可引起牙髓和根尖周病变，缺损过多可导致牙冠折断。其发病率为5~991%，患病率和缺损的严重程度随着年龄的增长而增高［1］。 为寻求一种较理想的充填方法，我科应用3M Z350纳米复合树脂、3M自酸蚀粘结剂配合排龈术对牙颈部楔状缺损进行修复，并对患者进行一段时间的追踪观察，对其进行临床疗效分析。 　　1材料和方法 　　11病例资料： 　　111病例来源和纳入标准：2009年6月~2010年6月来我院口腔科就诊的牙颈部楔状缺损患者60例，150颗，其中男性48颗，女性102颗，年龄30~65岁，前牙40颗，前磨牙80颗，磨牙30颗。纳入标准：牙颈部非龋损性缺损，深达牙本质中、深层，不近髓，对冷刺激敏感或轻度敏感，无充填体，无牙周病，牙髓活力正常，无咬合干扰。 　　12器械和材料：3M ESPE公司的FiltekZ350 XT纳米复合树脂（3M，USA）；3M Adper Easy One自酸蚀粘结剂（3M，Gerneny）;00-