HA纳米微粒对PVP低温保护剂的影响研究.pdfVIP

文章编号：CAR083 HA 纳米微粒对 PVP 低温保护剂的影响 郝保同 刘宝林 戎森杰 王欣 周国燕 （上海理工大学 生物热科学研究所 上海 200093 ） 摘 要 为了研究羟基磷灰石纳米微粒对低温保护剂性质的影响，本文利用 DSC 测量了含有不同浓度纳米微粒的 PVP 低温 保护剂的比热、玻璃化温度和反玻璃化温度。试验结果表明纳米微粒对玻璃化和反玻璃化温度有较为明显的影响，对比热的 影响不明显，但都随着纳米微粒的浓度增大而减小。对这一现象本文从纳米微粒与溶液之间的相互作用方面给出了解释。 关键词 纳米微粒 比热容 低温保存 玻璃化温度 DSC Hao Baotong Liu Baolin Rong Senjie Wang Xin Zhou Guoyan (Institute of Biothermal and Technology, University of Shanghai for Science and technology, shanghai 200093, china) Abstract To study the effects of the nanoparticles on thermodynamic parameter of PVP cryoprotective agents, the DSC were used to measure the specific heat, vitrification temperature and devitrification temperature of the PVP solutions with/without nanoparticiles in the paper. The result shows that the nanoparticles have significant impact on vitrification temperature and devitrification temperature, while the impact on the specific heat is not obvious. All of the three parameters decrease with the increasing of the concentration of nanoparticles. The mechanism was analyzed based on the interaction between the nanoparticles and solution. Keywords Nanoparticles Specific heat Cryopreservation Vitrification temperature DSC [5] 体的黏度影响比较大 ，有助于保护剂溶液加速降 1 引言 温速率，促进玻璃化转变。纳米微粒加入到低温保 护剂中，主要影响了低温保护剂的分子结构，进而 在冻结过程中控制低温保护剂中冰晶的形成 影响了纳米低温保护剂的在降温过程中比热、玻璃 对细胞、器官和组织的保存具有重要的意义。根据 化和反玻璃化温度的变化，关于这方面的研究还没 冰晶形成理论[1] ，与平衡冻结过程相比，有较大过 有见报道。 冷度的溶液在冻结过程中更加容易形成冰晶而非 玻璃化，虽然纳米微粒可以减小低温保护剂的过冷 2 实验方法与材料 度，但是纳米微粒的晶核作用也加速了冰晶的形 成，导致玻璃化能力下降。X. Han[2]等把纳米微粒