无机纳米材料对水中污染物的吸附去除性能研究.ppt

近期各期刊已发表的参考文献 二. 同步吸附多种无机微污染物纳米功能材料 2.氧化铁 /羟基氧化铝复合材料 二. 同步吸附多种无机微污染物纳米功能材料 3. 乙二醇钛纳米材料 Figure 1. (a) SEM image, (b) TEM image, (c) XRD and (d) BET with BJH method (insets) of the titanium glycolate. BET=246.5 m2.g-1 二. 同步吸附多种无机微污染物纳米功能材料 3. 乙二醇钛纳米材料 Figure 3. Adsorption efficiencies of As(V) and As(III) by titanium glycolate as a function of pH. Experiments were conducted at pH 2~10, with 5 mg samples stirring for 2 h. Initial arsenic concentration: 10 mg·L-1, sample volume: 25 mL. 二. 同步吸附多种无机微污染物纳米功能材料 3. 乙二醇钛纳米材料 Figure 4. (a) Change in aqueous Pb(II), As(V) and As(III) concentration with time, and (b) adsorption kinetics based on the pseudo-second-order kinetic model, C0 = 10 mg·L-1 and sample dose is 20 mg/100 mL; (c) Adsorption isotherms, (d) Langmuir isotherm, the initial ion concentration is 10~200 mg·L-1 and sample dose is 5 mg/25 mL. Table 1. Experimental and Calculated qe values, Pseudo-second-order rate constants (k2), and Correlation coefficient values (R2). The dosage of the Ti(OCH2CH2O)2 adsorbent was 0.2 g·L-1. Table 2. The maximum adsorption capacity (qm), Equilibrium constant (b), and Correlation coefficient values (R2). 二. 同步吸附多种无机微污染物纳米功能材料 3. 乙二醇钛纳米材料 二. 同步吸附多种无机微污染物纳米功能材料 3. 乙二醇钛纳米材料 Figure 5. (a) FTIR spectra of Ti(OCH2CH2O)2 with and without adsorbed heavy metal ions; High resolution XPS spectrum of (b) Pb(II)4f, (c) As(V)3d and (d) As(III)3d of titanium glycolate treated with 200 mg·L-1 of Pb(II), As(V) and As(III) aqueous solution at pH=4. 1. 基于富勒烯功能纳米材料的合成 三. 杀灭微生物微污染物纳米功能材料 1992年, Dr. McEwen (JACS) 提出 “自由基海绵（Ridcal Sponge）”的概念，即指C60分子对自由基的清除能力就像一块海绵一样，吸收力强而且容量超大。 富勒烯可抗链球菌感染 Tsao等, Antimicrobial Agent and Chemotherapy, 2001, 1788 富勒烯衍生物制备 Bingle-Hirsch 反应 优点： 溶解度高 分子间作用力强 生物相容性好 高压电源 储样器 喷头 接收装置 由纳米纤维组成的膜，具有比表面积大，均一性高、结构稳定性好 1. 基于富勒烯功能纳米材料的合成 三. 杀灭微生物微污染物纳米功能材料 静电纺丝技术基本原理 不同掺杂量C60衍生混合物与PAN复合薄膜材料的SEM 照片 a)2% b) 4% c) 6% C60衍生物/PAN复合膜材料的制备 a b c 标尺：100 nm PAN：聚丙烯腈 1. 基于富勒烯功能纳米材料的合成 三. 杀灭微生物微污染物纳米功能材料 PVP