pztnicuzn铁氧体复合双性材料电磁性能分析-analysis of electromagnetic properties of pzznuzn ferrite composite bi - material.docx

ABSTRACTABSTRACTThe continuous development of information society promotes the electronic components to the direction of small size, light weight, multi-functional and high stability. Thus put a variety of materials to carry out the special features composite, the component having a variety of functions has become the urgent needs of the market, it is become an important direction and hot spots to make the study of functional composite materials. At the present, the productions of many multi-functional components use LTCC (Low Temperature Co-fired Ceramic) technology. However, different dielectric layers rate mismatch between the densification rate, sintering shrinkage and thermal expansion, which restricts the industrialization process of cofired technology.In this thesis, the composite mechanism and the basic mechanisms of modification and low-temperature sintering of PZT-NiCuZn ceramic-ferrite composite materials have been analyzed. Then a series of novel materials and its preparation are explored and investigated. It is expected to become inductors, capacitors dual-performance materials. The main results are as follows:The effects of preparation process were researched on the microstructure andelectromagnetic properties of ceramics. The pre-sintering temperature, sintering temperature are changed regularly to investigate the variation of the phase formation by X-ray diffraction studies, the micrographs of the sintered ceramics by SEM, and the bulk density by Archimedes method. The frequency dependence of complex permeability, quality factor, and dielectric constant are studied.With the systemically analyses of the synthesis of ferroelectric-ferromagnetic composite materials, the low temperature sintered NiCuZn ferrites and perovskite PZT was chosen as the main components. The ferroelectric-ferromagnetic composite material is synthesized by usual ceramic technology with NiCuZn ferrites and perovskite PZT as the main components. The microstructure and electromagn