预分解窑煅烧白色硅酸盐水泥节能增白技术分析-analysis on energy saving and whitening technology of white portland cement calcined in precalciner kiln.docxVIP

ABSTRACTwhiteness. Moreover, the petroleum coke was in the use of low cost. Aiming at the problem of high combustion ignition, high combustion temperature and high sulfur content, we tried to solve them by mixing biomass fuel materials, adding alkali materials. The method of chemical removal of iron from the porcelain clay can effectively improve the whiteness of the porcelain clay, and iron removal rate was 40.9%. Compared with air cooling and water cooling technology of white cement in the physical and mechanical properties, they were similar in the intensity of 3d and 28d. Compared the clinker burn both in laboratory electric furnace and in YS , the whiteness of clinker under water cooling process was generally higher than that under air cooling process in 1~2 Hunter whiteness. There was no significant difference, and the difference mainly came from vitreous content and the Ca(OH) 2 content generated of mineral hydration. The whiteness of clinker increased with the increase of specific surface area, but the growth of whiteness was not the same rate as the fineness .Whenthe specific surface area was 550m2/kg, the whiteness would not basically improve.The fineness had a greater influence on the whiteness of cement, when the specific surface area was 600m2/kg, the whiteness was basically in a state of saturated.Key words: White Portland cement; whitening; cooling; energy conservation目 录第 1 章 绪论................................................................................................................... 11.1 选题背景与意义 ................................................................................................ 11.2 我国白水泥行业的生产发展与现状 ............................................................... 31.2.1 中空干法窑 .............................................................................................. 31.2.2 预热器干法窑 ........................................................................................... 41.2.3 预分解窑 ..............................................