双组分加成型室温硫化固体硅橡胶的制备及力学性能分析-preparation and mechanical properties analysis of two-component addition molding room temperature vulcanized solid silicone rubber.docxVIP

ABSTRACTpowderswouldbecakedbecauseofthebadcompatibilitybetweenthevinylsiliconeoilandtheordinaryquartzpowders.Modifiedquartzpowdershaveagoodlipophilicity,couldbewelldispersedinvinylsiliconeoil.Inthispaper,thetwocomponentaddition-curedRTVputtysiliconerubbercouldnotcakesavedforalongtime.Keywords:twocomponent;RTV;Additiontypeputtysiliconerubber;vinylsiliconeoil;mechanicalproperties目录第1章绪论··················································································11.1引言··················································································11.1.1有机硅·······································································11.1.2硅橡胶·······································································21.1.3硅橡胶的分类·······························································21.1.4高温硫化硅橡胶····························································21.1.5室温硫化硅橡胶····························································31.2双组分加成型室温硫化硅橡胶··················································41.2.1双组分加成型室温硫化硅橡胶的特点·································41.2.2双组分加成型室温硫化硅橡胶的用途·································51.3双组分加成型室温硫化固体硅橡胶的基本组成物质和硫化机理·········51.3.1基聚物·······································································51.3.2交联剂·······································································61.3.3催化剂·······································································71.3.4填料··········································································71.3.5乙烯基MQ硅树脂81.3.6抑制剂·······································································91.3.7双组分加成型室温硫化固体硅橡胶硫化原理························91.4双组分加成型室温硫化固体硅橡胶的研究进展···························101.5选题理论和实际意义····························································101.6课题研究内容·····································································11第2章双组分加成型室温硫化固体硅橡胶的制备·································122.1引言················································································122.2实验部分·······················