微量bi2o3掺杂znvtio基压敏陶瓷的分析-analysis of znvtio - based varistor ceramics doped with trace bi2o3.docxVIP

内蒙古科技大学硕士学位论文 III varistor voltage and the nonlinear property, they reduced from the peak value with 2413 V/mm and 45 at 800℃ to the minimum value with 98V/mm and 6.38 at 850℃. Quantitive activation analyses on the grain growth have been attempted by using the phenomenological grain growth kinetic. The obtained grain growth kinetic exponents and apparent activation energies for ZnVTiO based ceramics are2.39 and 190 KJ/mol. The results show that Bi2O3 dopants on ZnVTiO based varistor ceramics is an effectively the nonlinearity enhancers, if adding the properly sintering process, in the obtaining excellent varistor character the premise that can reduce sintering temperature at 750℃. Our results may pave a new way for the preparation of high performance ZnO varistor ceramics at low sintering temperature. Key Words：ZnO-V2O5-TiO2 based varistor ceramics;Bi2O3;microstructure;electrical nonlinearity -  PAGE 2 - 目 录 摘 要错误!未定义书签。 AbstractII  HYPERLINK \l _bookmark0 目 录- 1 -  HYPERLINK \l _bookmark1 1 绪 论- 1 -  HYPERLINK \l _bookmark2 1.1 压敏陶瓷- 1 -  HYPERLINK \l _bookmark3 1.2 ZnO 压敏陶瓷的制备- 2 -  HYPERLINK \l _bookmark4 1.2.1 原料的混合 - 3 -  HYPERLINK \l _bookmark5 1.2.2 烧结- 4 -  HYPERLINK \l _bookmark6 1.3 ZnO 压敏陶瓷的显微组织结构 - 5 -  HYPERLINK \l _bookmark7 1.4 ZnO 压敏陶瓷的??温烧- 6 -  HYPERLINK \l _bookmark8 1.5 ZnO 压敏陶瓷的导电机理 - 7 -  HYPERLINK \l _bookmark9 1.6 ZnO 压敏陶瓷的电性能参数 - 10 -  HYPERLINK \l _bookmark10 1.7 ZnVO 基压敏陶瓷的研究现状及存在的问题 - 11 -  HYPERLINK \l _bookmark11 1.8 本文研究难点、方案及意义- 13 -  HYPERLINK \l _bookmark12 1.8.1 研究中的难点及解决思路 - 13 -  HYPERLINK \l _bookmark13 1.8.2 研究内容以及技术路线- 13 -  HYPERLINK \l _bookmark14 1.8.3 实验设备- 14 -  HYPERLINK \l _bookmark15 1.8.4 研究的意义 - 15 -  HYPERLINK \l _bookmark16 2 试验方法 - 16 -  HYPERLINK \l _bookmark17 2.1 陶瓷制备工艺- 16 -  HYPERLINK \l _bookmark18 2.2 陶瓷相对密度的测试 - 16 -  HYPERLINK \l _bookmark19 2.3 陶瓷物相的分析 - 16 -  HYPERLINK \l _bookmark20 2.4 陶瓷显微形貌的观察 - 16 -  HYPERLINK \l _book