无机粉体防水材料研究.docVIP

无机粉体防水材料研究 　　摘要：以防水砂浆为技术依托，运用微细颗粒级配增密原理、复合叠加原理、混合化学物质和外加剂的作用等，研究出一种无机防水材料SH粉，参照《砂浆、混凝土防水剂(JC474-92)》标准，SH粉达到一等品。对发展防水材料在实际工程中应用具有一定的指导意义。 　　关键词：无机防水材料；砂浆；粉煤灰；硅粉；抗渗性 　　中图分类号：TU502 　　文献标识码：B 　　文章编号：1672-1683(2006)05-0034-03 　　 　　Research on the Inorganic Waterproof Material of SH Powders 　　LIU Ya-li，SUN Yong-bo 　　(Yellow River Engineering Consulting Co.，Ltd.，Zhengzhou 450003，China) 　　Abstact：Taken the waterproofmortar technology，used the dense increasing principles of particles grade，superposed the particles tocompound，andmixed the function ofchemicalmaterials and admixtures，this paper had developed a kind of inorganic waterproofmaterial SH powders. According to the standard of 《waterproof agent ofmortar andconcrete (JC474-92) 》，the quality of SH powderscan reach Grade A，which has a significance for the development of waterproofmaterials in practical projects. 　　Keywords：waterproofmaterials of inorganic；mortar；fly ash；silica；anti-permeability 　　 　　1 引 言 　　 　　在混凝土工程中，渗漏一直是困扰工程界的疑难病症，对防水材料和防水技术的研究一直是科研人员研究的重要课题。目前，我国防水材料的发展主要由两大类别组成：柔性防水材料和刚性防水材料。柔性防水材料主要是利用聚合和改性的有机高分子物质，铺在混凝土表面，形成一层憎水防水层，实现防水目的，是属于“治标”的外防水技术，虽其施工方便，但缺点是价格昂贵、有效期较短、变形较大、易从混凝土表面脱落、大多有毒等；柔性防水材料的应用较为广泛。刚性防水材料则是利用以水泥、砂、石子和少量外加剂等物质，在混凝土表面或内部形成致密的、有一定强度的、弥合混凝土结构缺陷的、增强混凝土防水性能的防水砂浆或防水混凝土，是属于“治本”内防水技术。其优点是价格低廉、耐久性好、与混凝土变形一致、便于修复等，但是其施工控制较为严格；刚性防水材料多用于大型刚性块体防水建筑物中。基于以上比较，本文针对水池、游泳池、水族设施、密封污水处理系统、沟渠、堤坝、地铁、隧道、坑道、室内地面、屋面、地下室等建筑物的防水，提出研究无机刚性防水材料课题，具有实际意义。 　　 　　2 原材料 　　 　　2.1 胶凝材料 　　水泥采用湖北黄石华新水泥厂生产的堡垒牌42.5普通硅酸盐水泥，其化学组成、矿物组分及物理性能见表1和表2；粉煤灰为Ⅰ级灰，其化学成分及性能见表3；硅粉的化学成分见表4。 　　 　　2.2 砂 　　本文采用细河砂，成型试件时，取砂的饱和面干状态。砂的细粉含量为1.7%，细度模数2.05。砂的其它性能见表5、表6。 　　2.3 混合的化学物质及外加剂 　　混合的化学物质及外加剂具有膨胀、激发和减水功能。 　　 　　3 试验设计思路 　　 　　以防水砂浆为技术依托，以提高砂浆的抗渗性和便于施工为目的，采用灰砂比为1∶2，砂浆的跳桌流动度控制在160mm左右，以测试砂浆7 d龄期的渗透高度作为比较依据，寻找各掺合料和外加剂对砂浆抗渗性影响的规律性，找出一种最优组分。然后按照《砂浆、混凝土防水剂(JC474-92)》规定，测试该最优组分的其它性能。 　　本文试验均是按《硅酸盐水泥、普通硅酸盐水泥(GB175-92)》、《水工混凝土试验规程(DL/T 5150-2001)》及《砂浆、混凝土防水剂(JC474-92)》的规定，做砂浆的抗渗试验、强度试验等其它测试试验。抗渗试验采用天津仪器厂生产的砂浆抗渗仪。在寻找规律阶段，对砂浆