混凝土高温后裂缝修复研究.docVIP

混凝土高温后裂缝修复研究 　　摘要：混凝土结构受火灾之后，不仅对混凝土本身性能产生巨大影响，由火灾等原因引起高温烧伤的混凝土强度随温度的升高明显降低，钢筋与混凝土的粘结力随之下降。本文对高温后的水泥砂浆、混凝土采取了不同的修复方式。通过X射线衍射分析、扫描电镜观察及强度的测定，以及经不同的修复方式修复后的过火水泥砂浆、混凝土的修复机理，从而得出了修复工艺对过火水泥砂浆、混凝土性能的影响规律。 　　关键词：水泥砂浆，混凝土，高温，修复，力学性能 　　Abstract: After the concrete stucture being destroyed by fire, there are not noly a huge impact on the performance of concret itselt, but also the the concrete strength lowering along with the increase of temperature, as well as the cementing bond of steel and concrete. In this paper, multiple repair methods are employed on the high-temperature cement mortar and concrete. By the analysis with X-ray diffraction, scanning electron microscopy and determination of strength, as well as the mechanism of multiple repair methods employed on the after fire cement mortar and concrete, the law of the repair techniques influencing the cement mortar and the performance of concrete is obtained. 　　Key words: cement mortar; concrete; high temperature; repair; mechanical properties 　　中图分类号：TJ414.+3 文献标识码：A 文章编号：2095-2104（2012） 　　1研究目的及意义 　　混凝土结构受火灾之后，不仅对混凝土本身性能产生巨大影响，由火灾等原因引起高温烧伤的混凝土强度随温度的升高明显降低，钢筋与混凝土的粘结力随之下降，混凝土温度达到300℃后抗拉强度下降50%，抗压强度下降60%，光圆钢筋与混凝土的粘结力下降80%，由于受热，混凝土体内游离水大量蒸发也可产生急剧收缩。混凝土具有热胀冷缩性质，当外部环境或结构内部温度发生变化，混凝土将发生变形，若变形受到约束，则在结构内将产生应力，当应力超过混凝土抗拉强度时即产生温度裂缝。温度裂缝又分为表面裂缝和贯通裂缝两种。这两种裂缝在不同程度上都属于有害裂缝。 　　因此，混凝土的裂缝问题一直是学术界和工程界所关注和研究的重大课题。裂缝的修复自然就成为国内外学者研究的热点问题。裂缝的修复技术及机理自然就成为国内外学者研究的热点问题。针对混凝土修复技术存在的问题，本文将探索和提出过火混凝土的损伤机理，并以此为理论依据，设计合理的修复工艺，对修复前后的混凝土通过X射线衍射分析及扫描电镜观察。探讨修复工艺对混凝土组成、强度等的影响规律。 　　2主要研究内容 　　(1) 在对大量国内外相关资料进行分析和通过实验的基础上，提出高温对混凝土的损伤机理； 　　(2) 设计出合理的修复方案：①浸入清水 ②浸入饱和水玻璃 ③涂刷水泥基渗透结晶材料 ，对受损试件进行修复； 　　(3) 通过对试件的力学性能等试验，研究修复工艺对过火混凝土的强度等的影响； 　　(4) 运用SEM和XRD等手段对混凝土内部产物进行微观分析（特别对新老混凝土界面）结合修补工艺及修补剂对过火水泥砂浆、混凝土成分、强度的影响及影响的机理进行研讨。 　　3混凝土的修复试验 　　(1) 清水修复 　　将标有A100、A300 、A500、A700（900℃高温后的试块完全呈酥碎状，以无修复条件）的试块各两块放入水槽中，试块互相不接触间隔大约1～2cm,向水槽中注满水。室温养护七天后取出。 　　 (2) 饱和水玻璃修复 　　将标有B100、B300、B500、B700的试块各两块放入带有底格的水槽中，试块互相不接触间隔大约2cm，像水槽中注满饱和水玻璃。室温养护七天后取出。 　　(3) 水泥基渗