高频拉铸工艺对锡磷青铜铸坯品质影响.docVIP

高频拉铸工艺对锡磷青铜铸坯品质影响 　　作者简介： 赵惠芬(1972-),女，工程师，主要从事铜合金生产加工技术的研发. 　　摘要： 研究了生产锡磷青铜采用短节距、高频率以及二次反推的牵引制度的高频拉铸工艺.结果表明:高频拉铸工艺可以细化铸锭晶粒、减少成分偏析和枝晶偏析,得到成分均一、组织均匀的优良铸锭,可减少后续加工的缺陷发生率,提高了生产效率. 　　关键词： 高频拉铸; 锡磷青铜; 组织性能 　　中图分类号：TG 339 文献标志码： A 　　Effects of the High Frequency Pull Casting on Phosphor Bronze Ingot 　　ZHAO Hui??fen, LI Guo??hua, DAI Jiao??yan 　　(Ningbo Jintian Copper(Group)Co., Ltd., Ningbo 315034, China) 　　Abstract： The high frequency pull casting of phosphor bronze was studied in the paper. This process is characterized by short pitch, high frequency and the second thrust reversers. The results show that high frequency pull casting can refine grains, diminish ingredient segregation and dendritic segregation, which helps to obtain a fine homogeneous ingot, reduce the defect rate in subsequent processing as well as greatly improve production efficiency. 　　Key words： high frequency pull casting; phosphor bronze; microstructure and properties 　　0 前言 　　锡磷青铜具有如下特点:高的弹性、耐磨性和抗磁性;在热态和冷态均可压力加工;焊接和钎焊性良好;切削性能好;在大气和淡水中抗蚀性好;铸造性良好.冷加工状态的锡磷青铜薄带材早已被广泛应用于无线电、电子和通信工业中制造具有高导电性的弹性零件,主要用于制造导电性能好的弹簧接触片和其他弹簧,精密仪器中的耐磨零件和抗磁元件,如接触簧片电刷盒和振动片等［1］. 　　锡磷青铜生产时,一直采用低频拉铸工艺,拉铸频率为14次/min,拉铸速度为168 mm/min,节距为12 mm,拉铸工艺为拉停退.拉1 s、停3 s,多数时间为停顿工序.CN 1263876C中提出的紫铜带拉铸工艺为小引程短停顿,中途适当加以反推的工艺过程,仍然是拉铸时间短,停顿时间长,拉铸速度慢,生产效率低.在此拉铸条件下,拉铸速度较慢,生产效率低,且普遍存在铸锭组织比较粗大、不均匀以及有成份偏析等现象.而不良的铸锭组织将对后道工序产生不良的遗传作用.本试验旨在寻求一种高效率,并能同时改善铸锭组织、减少成分偏析和枝晶偏析的拉铸工艺,为能快速得到优良的铸锭提供一定的生产经验. 　　1 试验方法 　　锡磷青铜高频拉铸工艺特征为铸造温度为1 050～1 080℃、拉铸冷却水压力为0.55～0.65 MPa,拉铸过程包括:向前拉铸第一次停第一次反推第二次停顿第二次反推第三次停顿.上述工序为一个单元循环的连续过程.拉铸速度提高至180～300 mm/min,拉铸频率提高至40～94次/min.拉铸速度包括从逐步加速拉铸过渡到恒速拉铸,拉铸频率包括从逐步加快拉铸频率过渡到恒定频率拉铸.高频拉铸工艺参数见表1.原拉铸工艺参数见表2.上海有色金属第35卷 　　第2期赵惠芬,等:高频拉铸工艺对锡磷青铜铸坯品质的影响 　　 　　表1高频拉铸工艺参数 　　Tab.1High frequency casting parameters 　　工艺拉速/ 　　(mm? 　　min-1)节距/ 　　mm频率 　　(次/min)周期/ 　　s拉距/ 　　mm拉时/ 　　s第一次 　　停顿时 　　间/s第一次 　　反推距 　　离/mm第一次 　　反推时 　　间/s第二次 　　停顿时 　　间/s第二次 　　反推距 　　离/mm第二次 　　反推时 　　间/s第三次 　　停顿时 　　间/s起拉9010115.510.0014.5―――――00