低密度聚乙烯蒙脱土纳米复合材料空间电荷特性研究电气工程专业论文.docx

重庆大学硕士学位论文英 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV showed that thermal aging made LDPE accumulate more space charge, and decreasing the dissipation rate of space charge after the removal of the applied voltage. The influence of space charge accumulation and dissipation of PE under hydrothermal condition was greater than that under dry-thermal condition. ④The accumulation and dissipation characteristics of space charges of LDPE/MMT were investigated based on the space charges testing system of pulse electro-acoustic (PEA) approach. According to the test result of differential scanning calorimetry (DSC) and dielectric frequency spectra, including space charge trap theory, the inhibition mechanism of added MMT nano-particles to restrain space charge in LDPE was explained. Experiments and analysis results showed that the addition of MMT nano-particles restrained the accumulation of space charge of LDPE under DC voltage, improved the rate of dissipation of space charge of LDPE after the removal of the applied voltage, and reduced the influence of space charge of cable for DC high voltage transmission. Key Words: Low density polyethylene, montmorillonite, nano-composites, Space charge, crystallinity state 重庆大学硕士学位论文目录 重庆大学硕士学位论文 目录 目 录 中文摘要I 英文摘要 II 1 绪 论 1 1.1 课题研究意义 1 1.2 聚合物/层状硅酸盐纳米复合材料的研究现状 2 1.2.1 聚合物/层状硅酸盐纳米复合材料研究概况 2 1.2.2 蒙脱土有机化改性进展 3 1.3 聚合物空间电荷研究现状 4 1.3.1 聚合物空间电荷理论 4 1.3.2 聚合物空间电荷测量技术 6 1.3.4 空间电荷影响因素与抑制措施 8 1.4 本文研究内容 10 HYPERLINK \l _TOC_250007 2 LDPE/MMT 纳米复合材料制备与性能测试 11 HYPERLINK \l _TOC_250006 2.1 LDPE/MMT 纳米复合材料制备过程 11 2.1.1 蒙脱土有机化处理 11 HYPERLINK \l _TOC_250005 2.1.2 熔融插层复合法制备 LDPE/MMT 纳米复合材料 12 HYPERLINK \l _TOC_250004 2.2 LDPE/MMT 纳米复合材料结构表征 13 HYPERLINK \l _TOC_250003 2.2.1 LDPE/MMT 纳米复合材料结构基本分类 13 HYPERLINK \l _TOC_250002 2.2.2 有机化蒙脱土 XRD 分析 15 HYPERLINK \l _TOC_250001 2.2.3LDPE/MMT 纳米复合材料 SEM 微观表征 16 HYPERLINK \l _TOC_250000 2.3LDPE/MMT 纳米复合材料性能测试 17 2.3.1 耐热性能 17 2.3.2 冲击强度 18 2.3.3 介电强度 18 2.4 本章小结 20 3 冷却介质对 LDPE 空间电荷输运特性的影响研究 21 3.1