退火工艺和成分对冷轧无取向电工钢性能的影响.pptVIP

退火工艺和成分对冷轧无取向 电工钢性能的影响 Effects of Annealing Process and Chemical composition on the Properties of Cold Rolled Non-Oriented Electrical Steel 主要内容：Main content: 随着钢铁冶金技术的进步，无取向电工钢的性能指标也不断提高。同时在当前日益激烈的市场竞争条件下，钢铁企业对节约资源、降低成本、提高产品质量等意识的增强，因此在成分一定的条件下，如何最大程度的提高无取向电工钢成品性能也成为企业和科研工作者研究的重点。 Along with the iron and steel metallurgy technology progress, non-oriented electrical steel performance index is also increased. Under the fierce competition market conditions, steel company consciousness-raising in save resources, reduce costs, improve product quality. How to improve the property under the given composition is a keystone for company and scientific researcher. 概述—电工钢性能影响因素Summary—The factor influence 论文的研究内容The content of this paper 实验成分及方法Chemical composition and method 实验方法： Experimental method: 采用实验室马弗炉，模拟无取向电工钢的退火工艺过程。退火工艺如下: Simulate the non-oriented electrical steel annealing process by laboratory muffle furnace 性能检测结果Result 试验结果分析 Result and Analysis 硅含量对无取向电工钢性能的影响 Effects of silicon composition on the iron loss of non-oriented electrical steel 试验结果分析 Result and Analysis 退火工艺对无取向电工钢性能的影响： Effects of annealing temperature the properties of cold rolled non-oriented electrical Steel 试验结果分析 Result and Analysis 试验结果分析 Result and Analysis 退火温度对冷轧无取向电工钢磁感的影响 Effects of annealing temperature on the iron loss of non-oriented electrical steel 试验结果分析 Result and Analysis 组织检测Structure 组织检测Structure 试验结果分析 Result and Analysis 讨论分析 Discuss and analysis  1、硅含量越高成品铁损越低 The higher silicon the lower iron loss 讨论分析 结论Conclusion  1、在一定范围内升高退火温度，晶粒尺寸增加，铁损降低，继续升高退火温度，铁损变化不明显。 the grain size increased and the iron loss reduced in a certain range with increasing annealing temperature, continue to increasing the annealing temperature, the iron loss changed not obvious. 2、延长保温时间，晶粒尺寸变化不明显，但均匀性提高，在低温段退火时增加保温时间，铁损降低，高温段退火时增加保温时间，铁损变化不大，磁感与退火时间无变化无明显规律。 The grain size changed not obvious with prolonging annealing time, but it became more uniformity. The ir