高蠕化率蠕墨铸铁热分析分析-材料加工工程专业论文.docxVIP

 PAGE 5 ABSTRACT TEU between 1130℃ and 1143℃, TER between 1150℃ and 1153℃, the graphit -e is a worm and ≤50% ductile, which is compacted graphite iron; when T EU between 1130℃ and 1143℃, TER between 1143℃ and 1150℃, the graphite is worms and 50% ductile, which is ductile iron. Combined with the overall shape of the entire thermal analysis to determine the graphite morphology, pre- liminary result is that when integrated parameter M less than 10, the shape s- ubstantially similar thermal analysis, graphite morphology similar. Ti also carried out late on the ball of the nodularity impact test, Ti is a kind of antiball elements, can reduce the residual amount of hot metal ball el - ements of graphite worms. Preliminary results; With increasing Ti content, the ball of tissue sample rate increased first downward trend, and when the additi - on amount of Ti ball at the highest rate of 0.0595 percent, the lowest rate of creep, continue to add Ti ball rate downward trend. Key Words：thermal analysis；Characteristic temperatures；thermal analysis cure； nodularity；Ti 目 录 目 录  HYPERLINK \l _bookmark0 第 1 章 绪论 1  HYPERLINK \l _bookmark1 1.1 引言 1  HYPERLINK \l _bookmark2 1.2 蠕墨铸铁的发现和发展 5  HYPERLINK \l _bookmark3 1.3 蠕墨铸铁的控制及处理 9  HYPERLINK \l _bookmark4 1.4 现有检测方法 10  HYPERLINK \l _bookmark5 1.5 热分析方法的应用及发展现状 11  HYPERLINK \l _bookmark6 1.6 论文研究的主要内容 15  HYPERLINK \l _bookmark7 第 2 章 热分析方法研究 16  HYPERLINK \l _bookmark8 2.1 热分析系统 16  HYPERLINK \l _bookmark9 2.2 热分析样杯的制备 16  HYPERLINK \l _bookmark10 2.3 热分析曲线和特征值 17  HYPERLINK \l _bookmark11 2.4 试验材料 18  HYPERLINK \l _bookmark12 2.4.1 原铁水成分要求 18  HYPERLINK \l _bookmark13 2.4.2 蠕化剂 19  HYPERLINK \l _bookmark14 2.4.3 孕育剂 19  HYPERLINK \l _bookmark15 2.4.4 球化剂 20  HYPERLINK \l _bookmark16 2.4.5 试样凝固组织金相分析 20  HYPERLINK \l _bookmark17 第 3 章 冲入法和喂丝法试验及结果 21  HYPERLINK \l _bookmark18 3.1 冲入法处理 21  HYPERLINK \l _bookmark19 3.2 冲入法试验结果 24  HYPERLINK \l _book