激光冲击镁合金接头疲劳裂纹扩展数值模拟计算力学专业论文.docxVIP

激光冲击镁合金接头疲劳裂纹扩展数值模拟Numerical 激光冲击镁合金接头疲劳裂纹扩展数值模拟 Numerical Simulation of Laser Shock Peening on Fatigue Crack Growth of Magnesium Alloy Joint Abstract As representative of the lightweight metal，magnesium alloy has attracted widespread attention because of its superior mechanical properties．At present，in some industries that have higher quality requirements such as aviation，aerospace，automobile and other industries， there is an increasing demand for magnesium alloys．However,some disadvantages of magnesium alloy itself such as poorer anti—fatigue performance，weldability and corrosion resistance，limit the possibility of谢de application．Therefore，it is of great significance to improve the mechanical performance of magnesium alloy．Currently,most researches on magnesium alloy are related to fatigue crack propagation after welding or fatigue crack propagation after laser shock peening(LSP)，and there are few studies on the combination of welding，LSP processing and fatigue crack propagation analysis．Therefore，it is of great significance to study in this respect． In this paper,based on the finite element analysis software ABAQUS 6．12—1／Explicit， multi-pass welding of butt joint and T-joint of thick plate is simulated．The shape of the heat source and moving load are implemented into SUBROUTINE DFLUX using Fortran language，and life and death unit technology is used to realize the finite element simulation of multi-pass welding，and C3D8T unit(thermal-displacement coupling unit)is used to calculate the temperature field and residual stress field at the s锄e time．Simulation results show that the residual tensile stress in weld zone and heat affected ZOlle of the welding joint are relatively larger,and the residual stress Can seriously influence the service life of the welded joint． The finite element simulation of LSP of welded joint is further carried out．Because LSP is conducted at the high strain rate，the constitutive relations of quasi static will be no longer applicable in this