PAGE IV PAGE IV 题目：镍催化剂催化丙交酯开环聚合研究 　　　　　　　 PAGE I 镍催化剂催化丙交酯开环聚合研究 摘 要 以氧化锌或锌酸亚锡为催化剂催化乳酸单体制备丙交酯，研究反应时间和不同催化剂对丙交酯产量的影响。再以无水乙醇和乙酸乙酯对粗品丙交酯进行重结晶提纯。 再以二亚胺镍为催化剂进行D,L-丙交酯开环聚制备聚乳酸，研究催化剂用量、反应时间和反应温度对聚合反应的影响。 在本课题的实验条件下，粗品丙交酯产量高达80%，重结晶后丙交酯产量高达31.6%；在[M]/[I]=500/1时，140℃反应24h，聚乳酸的产率达到最高值90.4%。采用傅里叶变换红外光谱、差示扫描量热法对聚合产物进行表征。 关键词：乳酸单体；D,L-丙交酯；二亚胺镍；氧化锌；辛酸亚锡；环聚合 Nickel Catalyst for the Ring-opening Polymerization of Propylene Abstract Catalyst zinc oxide or zinc stannous Catalytic Lactic acid monomer propionic Lactide, researching the impact of reaction time and different catalysts on lactide ester production. Then using ethanol and ethyl acetate to purify the crude lactide by recrystallization. Then using diimine nickel as catalyst Catalytic D, L-lactide ring-opening polymerization method for producing a polylactic acid, Researching the reaction of the amount of catalyst ,reaction time and reaction temperature on the polymerization. Under the experimental conditions of this topic,the yield of the crude lactide yield is up to 80%,After recrystallization the yield of lactide is up to 31.6%;At [M]/[I]=500/1,140℃ and 24h, the yields of polylactic acid have the highest value of 90.4%.The structure of the obtained polystyrene was characterized using Fourier transform infrared spectroscopy differential scanning calorimetry. Keywords: lactic acid monomer; D, L-lactide diimine nickel; stannous octoate or zinc oxide; ring-opening polymerization 目 录 TOC \o 1-3 \h \z \u 2205 1 绪论 1 478 1.1概述 1 5631 1.1.1国内外发展史及研究现状 1 17760 1.1.2展望发展前景 4 29090 1.2聚乳酸的性能 4 1181 1.2.1基本性能 4 28569 1.2.2生物相容性 5 16719 1.2.3降解性能 5 22753 1.3聚乳酸的合成方法 6 24062 1.3.1直接缩聚法 6 21848 1.3.2开环聚合法 7 23719 1.4丙交酯的合成方法 8 14936 1.4.1丙交酯的纯化 9 21336 1.4.2影响丙交酯产率的因素 9 2891 2 实验部分 10 20237 2.1实验仪器 10 9132 2.2 实验药品 10 24078 2.3测试与表征 11 32344 2.4合成丙交酯 11 1691 2.4.1丙交酯的合成实验步骤 11 27675 2.4.2丙交酯的纯化 11 21427 2.4.3丙交酯的产率计算 11 23508 2.4.4产物纯度的检测 12 12584 2.5聚乳酸的合成 12 10418 3 实验分析