PMMA/EG导电复合材料的制备及性能测试 摘要：膨胀石墨由膨胀片化的石墨粒子组成，粒子内存在许多空洞或缝隙，有利于形成单体的GIC。通过原位聚合方法，即可制得聚合物插入石墨复合材料。本文将介绍以甲基丙烯酸甲酯（MMA）（EG）关键词：膨胀石墨，石墨层间化合物，原位聚合，石墨复合材料，甲基丙烯酸甲酯 Abstract：Expandable Graphite constitutes with particle of expanded graphite, as which exists some inanition or aperture , it’s tend to come into being the GIC of monocase. Composite material with polymer insert into the layer of graphite will be obtained by the technology of in-situ polymerization. This article will introduce a method of in-situ crystallization which obtains character Polymer/EG composite material ordered with PMMA insert into the layer of EG, then research the characteristic of configuration , mechanics and electrics. Keywords： expandable graphite，GIC，in-situ polymerization， graphite/polystyrene composite material，MMA 引言 导电复合材料 1 实验部分 1.1实验原理 1.2实验仪器 1.3实验药品 1）膨胀石墨 膨胀率约为250倍 2）甲基丙烯酸甲酯（MMA） 试剂纯 3）甲苯 试剂纯 4）偶氮二异丁腈 （AIBN） 试剂纯 5）无水硫酸钠（NaSO4） 试剂纯 6）无水乙醇 试剂纯 1.4实验方法和主要步骤 1)膨胀石墨的制备 2)精制 ①洗涤： ②减压蒸馏： ③AIBN（偶氮二异丁腈）的精制 3）膨 X-Ray衍射与红外测试 力学性能测试样条的制作. 6)电学性能测试 7) 电镜照片（sem） 1.5 实验中出现的问题： 药品回收： 倒吸： …… …… 2 实验结果与讨论 2.1产率及石墨含量 2.2力学性能的数据分析与讨论 2.3 电镜照片 2.4 X-Ray衍射谱图 2.5红外谱图 2.6 电学性能测试 3 结 论 1．对于PMMA/EG复合材料，随膨胀石墨含量的增加，其机械性能相应的增加，但其机械性能会受到板制作工艺的制约。 2. 单纯的膨胀石墨中的石墨薄片与复合体系中的石墨薄片的晶体结构是相同 的 ,也即尽管甲基丙烯酸甲酯在膨胀石墨内部的薄片间发生原位聚合 ,但它并没有改变石墨的晶体结构。 3. 通过透射电镜可以看到混炼的PMMA/EG复合样品中石墨以大量的纳米薄片分散于基体中,薄片的厚度大多为20～40ｎｍ参考文献： 王文平。中国科学技术大学博士学位论文。合肥，2003，8 朱继平。可膨胀石墨稳定性研究。合肥：合肥工业大学学报（自然科学版） 陈大为。2003年学士学位论文。 4．周祖福。复合材料学.武汉：武汉工业大学出版社，2002，11 5．吴人杰。复合材料.天津：天津大学出版社，2000，12 6．谢有赞。罗竣坤。不同的原子及基团对碳石墨材料性能的影响.碳素，1994，No.4 7．阎万明。膨胀石墨的性质及应用.内蒙古石油化工，第十九卷 8．吴翠玲，翁文桂，陈国华。膨胀石墨的多层次结构.华侨大学学报（自然科学版），Vol24，No.2，2003，4 9. 康飞宇。石墨层间化合物.新型炭材料，Vol15，第四期，2002，12 10.陈国华，翁文桂，吴大军等.石墨与聚苯乙烯的纳米复合过程研究.高分子学报，第6期， No. 6 2001，Dec 山东化工职业学院毕业论文（200年月） - 1 - 楷体，三号，加粗 页眉设置为(山东化工职业学院毕业论文字样,楷体,小五), 宋体 五号 正文的大标题都用仿宋体（三号） 各部分大标题下的小标题都用黑体（小四）， 各小标题下的具体内容用宋体（小四） 这一部分具体内容用楷体（五号） Times New Roman五号 “参考文献