PP%2f木粉复合材料注塑发泡成型的研究.pdfVIP

PP／木粉复合材料注塑发泡成型的研究 张军何继敏薛平 (北京化工大学塑料机械及塑料工程研究所，北京，100029) 摘要：采用普通注塑成型法制备了PP／木粉复合发泡材料，考察了发泡剂、相容剂及增韧剂的含量 对PP／木粉发泡材料力学性能、断面微观结构及表观密度的影响。结果表明：AC发泡剂对试样的密 度及泡孔形态影响较大；相容剂PP—g-MAH的加入很好地改善了复合发泡材料的界面相容性、力学 性能和木粉的分散性；随着增韧剂含量的增加，试样的冲击强度明显提高。 关键词：注塑、发泡、PP／木粉 RESEARCHONlNJECTIONFOAMING OF PP／WOODFLOURCOMPOSITES Jun，HeJimin，Xue Zhang Ping ofPlastic and ofChemical (Institute Machinery University Engineering，BeOing 100029，China) Abstract：PP／woodflourmicrocellularwas traditional compositepreparedby injectionmolding．The effectsofcontentof and on and agentdensity，mechanical foamingagent，compatilizertoughening property the were showedthat：influencesof of microstructureof studied．Theresults dosagesblowing composites on are hada effectontheinterfacial agentfoamingqualityveryimportant；PP·-g·-MAHpositive the of andincreasedmechanical thePP／woodflour and compatibilization properties compositesdispersing ofwood theincreaseof the ofthe increased effect flour；with tougheningagenhimpactstrengthcomposite noticeably． flour Keywords：injection，foaming，PP／wood 前言： 木塑复合发泡材料其内部均匀地分散着无数微小泡孔，可以有效降低材料的密度，木质纤维的加 入可以起到降低成本的作用。目前木塑发泡复合材料的成型方法主要有模压成型、挤出成型和注塑 成型等，其中模压成型和挤出成型已取得了阶段性的成果，而注塑成型是一个崭新的研究领域，还 处于探索阶段，但是注塑成型的木塑复合发泡制品已经凸显出其优点，如与挤出成型的木塑复合发 泡制品相比，其制品的外观和质感更酷似木材，具有更低的吸水率，注塑发泡成型过程中由于保压 时间和冷却