混凝土的渗透性经时变化规律的研究.pdfVIP

混凝土的渗透性经时变化规律研究 方永浩，岑奕侃，赵 伟，安普斌 （河海大学材料科学与工程学院，南京210098 ） 摘要 用自行设计的混凝土渗透试验装置研究了混凝土渗透参数的演变规律。发现在压力水作用下，混凝土在短 时间内渗透速率达到最大，随后就逐渐降低并趋向于稳定值。根据试验结果提出了混凝土渗透系数的时变模型。 关键词 混凝土 渗透 混凝土渗透试验装置 时变模型 中图分类号: T528 文献标识码: A Study on the Time－Dependent Change of Permeability of Concrete CEN Yikan，FANG Yonghao ，ZHAO Wei ， AN Pubin (College of Materials Science and Engineering, Hohai University, Nanjing 210098) Abstract In the present work, the law of permeability change of concrete subjected to hydraulic-pressure was studied using a self-designed concrete permeability testing device. The results show that when subjected to hydraulic-pressure, the permeating rate of the concrete increases to the maximum in a short time, and then gradually decreases towards a stable value. A time-dependent model for concrete subjected to hydraulic-pressure is proposed. Key wards concrete permeability concrete permeability testing device time-dependent model 碎石及自来水按表 1 所示配合比配制混凝土，成型成内、外直 0 引 言 径分别为 30 mm 和 110 mm的圆筒形试件，每组试样成型六个， 渗流溶蚀是水工混凝土构筑物破坏的主要形式之一。水工混 其中两个用于渗透试验，三个用于强度测定，另一个备用。试 凝土在水压力的作用下，会发生渗透和渗流，后者会引以混凝 件在混凝土标准养护室养护 28 d后，用切割机将试件两头截去， 土中水泥石组成的溶蚀破坏，因此渗透性是水工混凝土构筑物 得到高度为 110 mm的试件。取其中三个试件测定混凝土试件抗 中最为关注的特性之一。由于混凝土的水渗透性较低，通常用 压强度，结果见表 1。 混凝土在特定试验条件下能承受的（水不渗透）最大或在一定 水压下持续一段时间后的渗透高度来表征混凝土的抗水渗透性 表 1 混凝土试件配合比和抗压强度 能[1]，也有用气体渗透性表征渗透性的[2-3] ，而对混凝土渗透以 Table 1 Mix propo