振动消失模铸造球墨铸铁凝固组织转变的研究.pdfVIP

中国机械工程学会铸造分会第十一届消失模与V 法铸造学术年会论文集 振动消失模铸造球墨铸铁凝固组织转变研究 ∗ 肖伯涛 樊自田 龙威 宗晓明 （华中科技大学材料成形与模具技术国家重点实验室） 摘要：采用振动消失模铸造方法制备了球墨铸铁试样，分析研究了振动对消失模铸造球墨铸铁 凝固组织的影响。结果发现：在振动凝固球墨铸铁中，随试样厚度的增加，石墨球的数量增多、尺 寸减小，碳化物含量降低，而在静止凝固球墨铸铁中，随着试样厚度的增加，石墨球数及碳化物的 含量减少。此外，不管是振动凝固试样，还是静止凝固试样，牛眼状组织的数量均随试样厚度的增 加而增多。这主要应归因于振动在凝固金属熔体中引入了周期性的“压力-拉力” 。 关键词：消失模铸造；振动凝固；铁合金；微观组织 中图分类号TG249.6 Microstructures transformation of ductile cast iron in lost foam casting with vibration Xiao Botao, Fan Zitian, Long Wei, Zong Xiaoming （State Key Laboratory o f Material Processing and D ie Mould Techno logy, Huazhong University of Science and Technology ） Abstract: The ductile cast iron was prepared by lost foam casting (LFC) with mechanical vibration, and the effect of vibration on their microstructures was investigated. The results indicated that the amount of graphite nodule increases and its size decreases with the increasing of specimen thickness while the content of carbide reduces. Besides, the amount of bull’s eye structure increases in the specimen with and without vibration. The reason is that the periodicity “tension-pressure” occurred caused by vibration introduced in the molten metal. Keywords: Lost foam casting (LFC); Vibration solidification; Ferroalloys; Microstructures 消失模铸造技术（LFC ）是一种近无余量、精确成形的新技术，适合生产复杂零件，被称为是“代 表21 世纪的铸造新技术”和“铸造中的绿色工程”[1-6]，广泛用于铸铁、铸钢等黑色合金的铸造。但消 失模铸造的浇注温度较传统铸造高，且造型材料采用干砂，其传热速度慢，使得铸件的组织粗大， 力学性能较差。因此，细化消失模铸造铸件组织，提高其性能是发展消失模铸造技术需要解决的关 键问题之一。 振动凝固是一种细化铸件晶粒组织、提高铸件力学性能的有效方法，其原理是在金属凝固期间 施以外力（如机械振动、超声波振动、电磁振动等），使液体内部的枝晶在增大的过冷度、粘性剪切 力等作用下碎化、熔断，游离激冷晶的数目增加，达到细化晶粒之目的[8-10] 。综合比较各种振动方法， 机械振动具有操作简便、设备精度要求低、提高铸件质量效果明显等优点，是一种廉价、高效的细 ∗ 第一作者简介：肖伯涛(1978-), 男, 呼伦贝尔人, 博士研究生。 通讯作者简介：樊自田(1962-), 男, 教授, 博士生导师。