DP590钢原始奥氏体晶粒统计方法及初始晶粒尺寸模型.pdfVIP

DP590 钢原始奥氏体晶粒统计方法及初始晶 粒尺寸模型* 徐耀文 唐 荻 宋 勇 （北京科技大学高效轧制国家工程研究中心 北京 100083 ） 摘要：本文提出一种统计原始奥氏体晶粒尺寸的新方法。通过采用 Photoshop 和 Image-Pro Plus 软件，可以方便获得原始奥氏体晶粒直径、晶粒面积、晶粒尺寸分布等信息。为了对 Beck 公式 中的初始晶粒尺寸进行量化，研究了加热温度和加热速率对DP590 钢奥氏体晶粒尺寸的影响。 提出了以加热温度和加热速率为参数的奥氏体初始晶粒尺寸模型。结果表明，实验值与计算结 果吻合较好，模型准确可靠。 关键词：原始奥氏体 晶粒尺寸 初始 模型 DP590 Abstract ：A novel method was proposed to count prior-austenite grain size. Information such as grain diameter, grain area and grain size distribution can be drawn conveniently by using the software of Photoshop and Image-Pro Plus. In order to quantify the initial grain size in Beck equation, the effects of heating rate and soaking temperature on austenite grain size of DP590 were investigated. A model for initial grain size as a function of temperature and heating rate was developed. The good agreement between the predicted value and experimental data shows the reliability of the proposed model. Key words ：prior-austenite ， grain size ， initial ，model ，DP590 0 前言 D n D n Kt (1) 0 双相钢以其较高的强度和较好的成型性 式中，D 是最终的奥氏体晶粒直径；D0 是当 能被广泛应用于汽车制造业[1] 。钢在轧制的过 保温时间 t=0 时的奥氏体晶粒直径；n 是晶粒 程中，轧制参数会大大影响钢材的组织形式， 长大的时间指数；K 是与材料相关的常数。为 而不同的组织又决定了最终的力学性能。较小 了确定n 值，通常做法是忽略 D0 值，对式(1) 的原始奥氏体晶粒有利于轧后相变形成细小 两边取对数。然而根据最近的研究表明[3, 5]， [2] 的室温组织 。 随意忽略D0 对最终的 n 值求解是有影响的， 奥氏体晶粒长大模型可以对轧制过程进 尤其是当 D 值不是很大的情况下。 行指导，很多学者做了相关的建模工作[3-6] 。 根据 ASTM E 112[9] 的标准，有多种确定 描述奥氏体晶粒长大模型的经典的经验模型 奥氏体平均晶粒直径的方法。但是这些方法得 是 Beck 方程[7, 8] ： 出的不够稳定，人为因素对结果的干预较大，