两种无碳钢包砖应用对比的分析.pdfVIP

1两种无碳钢包砖的应用对比分析 1 2 2 2 黄家凯 李雪冬 罗三峰 多志军 (1 ．首钢京唐钢铁联合有限责任公司；2 ．濮耐集团股份公司) 摘 要 本文针对本公司所使用的两种无碳钢包砖进行了研究，对其理化性能和物相组成进行分析。对钢包砖用后 残砖进行分析。采用扫描电子显微镜研究了其在使用前后的显微形貌变化。通过对比探讨了这两种钢包砖在使用过 程中变化，探讨损毁机理。通过总结该两种钢包砖的特点，为正确合理选用无碳钢包砖提供了参考依据。 关键词 钢包砖 无碳砖 显微结构 The Application Comparative Analysis of Two Kinds of Non-carbon Ladle Brick Huang Jiakai1 Li Xuedong1 Luo Sanfeng2 Duo Zhijun2 (1. Shougang Jingtang Integrated Iron and Steel Co., Ltd.；2. Puyang Refractories Group Co.,Ltd.) Abstract This paper is about the study of two kinds of non-carbon ladle brick, it takes the analysis of their physical and chemical properties and phase composition by scanning electron microscope, which shows the microscopic appearance changes before and after on residual ladle brick. By comparative analysis, we discussed the changes in service and their damage mechanism, which provided the reference basis for the choice of non carbon ladle brick by their different characteristics. Key words ladle brick, non carbon brick, microstructure 随着冶金技术的不断进步，各种高性能钢种不断被开发出来。(超)低碳钢以其优异的性能，在汽车、家 电、电力等行业的应用也越来越广。炼钢生产过程中，钢包冶金是(超)低碳钢生产过程中非常关键的过程之 一。虽然(铝)镁碳钢包砖以其优异的抗侵蚀性和热震稳定性，广泛应用于钢包工作衬。但是含碳钢包砖在使 用过程中，会造成钢水增碳。为了满足(超)低碳钢生产的需要，减少钢水在生产过程中的增碳，无碳钢包的 应用也越来越广泛[1~3] [4~5] 。目前钢包无碳砖一般可以采用浇注料预制块和机压无碳砖等 。这些砖在使用时各 有其特点，在不同冶炼条件下表现出的使用效果也不同。 为了研究不同无碳砖的损毁机理，本文采用扫描电子显微镜分析等手段，对目前在 300t 钢包上使用的 两种无碳钢包砖进行了研究，通过对比其常规理化指标以及使用前后的显微结构，对该两种无碳钢包砖的特 点进行了分析探讨，为正确合理选用无碳钢包砖提供参考依据。 1 理化性能与使用效果对比 将钢包砖分别命名为 1 号、2 号，用切割机取部分钢包砖样品，经破碎、粉磨后分别进行 XRF 化学成 分分析和 XRD 物相衍射分析，研究其化学组成和物相组成，表 1 为两种钢包砖的化学分析结果和物相组成。 黄家凯，男，本科，工程师，从事钢铁用耐火材料管理，luyetao@