连铸板坯表面纵裂的成因分析及改进措施.pdfVIP

( ) 1 9 9 7 年 1 1 月 钢　铁　研　究 第 6 期 总第 99 期 N ovem ber　1997 R esearch on Iron Steel N o. 6　 (Sum 99) 连铸板坯表面纵裂的成因分析及改进措施 周　有　预 (武钢钢研所) 摘　要　对连铸板坯表面纵裂的成因进行了一系列的分析研究。查明浸入式水口在注中损坏 和结晶器用保护渣的性能不合是主要原因。采用相应的改进措施后, 该类缺陷的发生率大幅度降低。 关键词　连铸板坯　表面纵裂　浸入式水口　结晶器保护渣 THE ANALY SIS FOR THE CAUSE OF SURFACE CRACKS IN CONTINUOUS CAST SLAB AND THE COUNTERM EASURE Zhou Youyu ( Iron steel R esearch Institute W ISCO ) Synopsis　T h is paper analyses and studies the cause of sruface crack s in continuous cast . slabs T he m ain causes of the defects w h ich are investigated are the dam age of the subm erged noz zle during casting and som e undesirable p roperties of the mould pow der. T he occurrence of such . defects are successfully decreased by app lying the co rresponding counterm easures 　 　 　 　 Keywords continuous casting slab surface crack s subm erged nozzle mould pow der 则贯穿整块铸坯的定尺长度, 达 9. 8 。 m 1　前　言 采用磁粉探伤法探测了 4 块有该类缺陷 某钢厂在一段时间内生产的连铸板坯, 的铸坯, 判定该缺陷为表面纵向裂纹。在确认 其宽面出现了纵向裂纹, 用该批板坯轧出的 了裂纹的范围后送热轧加热炉按常规加热制 板材在相应部位带有纵向线形缺陷。为了查 度加热, 出炉冷却后再次探测, 结果显示: 加 明连铸板坯表面纵裂的成因, 组织攻关组进 热后铸坯上的裂纹范围与加热前基本上相对 行了分析研究。