连铸方坯表面裂纹的控制.pdfVIP

　第 3 1卷 　　第 5期 金 　　属 　　制 　　品 2005 年 10 月 　Vol31　　 No5 Steel W ire Products October 2005 连铸方坯表面裂纹的控制研究 齐新霞 　黄 　重 ( 安阳钢铁集团有限责任公司 　455004) 摘 　要 　对 30M nSi连铸方坯表面横裂纹产生的原因进行了分析 。提出工艺优化措施 :采用转炉炼钢 ,连铸拉速控 制在较高水平 ,结晶器水量增加到 106～120 m3 / h,并对其结构进行改进 ,生产出无缺陷铸坯 ,使 30M nSi盘条的正 品率由 87. 74%提高到 99. 59% 。 关键词 　连铸方坯 ;横裂纹 ;工艺优化 Con trol Research of Crack on the Surface of Con tinuou s Ca sting B illet Q i X inx ia 　Hu a n g Zho n g (A ny ang Iron and S teel Group Co. , L td. 　455004) A b stract　To analyze the cau se for horizon tal crack on the su rface of 30M nSi con tinuou s ca sting b illet. Op tim ized p rocess m easure s are p ut forward: steelm ak ing u se s BOF, draw ing sp eed of con tinuou s ca sting is controlled at h igher lever, water 3 flux of crystal un it is increased to 106～120 m / h and its structu re is imp roved in order to p roduce nondefect ca sting b illet. Quality good s rate of 30M nSi w ire rod increa se s from 87. 74% to 99. 59%. Keywords　con tinuou s ca sting b illet; horizon tal crack; p rocess op tim ized 1　铸坯表面横裂纹产生原因 安钢 100 t 电炉 →L F →150 mm ×150 mm 生产线 所生产的 30M nSi方坯表面角部存在横裂纹缺陷 ,横 裂纹产生于结晶器初始坯壳形成振痕的波谷处 ,振 痕越深 ,横裂越严重 。横裂纹形貌如图 1所示 。 图 2　30M nSi钢中氮的质量分数 铸坯开裂 。对 2004 年 2—3 月份生产的 30M nSi统 计显示 ,铸坯表面横裂纹炉次的钢水成分中铝含量 均偏高 ,尤其是钢中氮含量高时更易使铸坯表面产 生横裂纹 。 1. 3　结晶器