制备方法对镧钡共改性氧化铝性能的影响.pdfVIP

第24卷第6期 无 机 化 学 学 报 Vo1．24 No．6 2008年6月 CHINESE JOURNAL OF INORGANIC CHEMISTRY 998-1O02 制备方法对镧钡共改性氧化铝性能的影响 董文萍 张丽娟 温怡芸 陈耀强 龚茂初 (四川大学化学学院，成都 610064) 关键词：氧化铝；氧化钡；氧化镧；制备方法 中图分类号：O614．33 l；0614．23*3 文献标识码：A 文章编号：1001--4861(2008)06—0998-05 一 Effect of Preparation Methods on Property of La，Ba Co-modified Alumina DONG Wen—Ping ZHANG Li—Juan WEN Yi—Yun CHEN Yao—Qiang GONG Mao—Chu (College ofChemistry,Sichuan University,Chengdu 610064) Abstract：The effect of preparation method on the properties of alumina modified by La203 and BaO was investigated by means of Low temperature nitrogen adsorption—desorption，NH3_TPD，NO—TPD and XRD．The results show that alumina prepared by peptizing method exhibits the best textural properties，alumina obtained by CO-preci[Iitation method presents the strongest surface acidity and alumina derived from impregnation method shows the best ability of NO adsorption．After calcination at 1 100 oC，all alumina except that from impregnation method have excellent thermal stability．When the specific surface area and pore volume of alumina are large enough，the activity of catalyst Pd／alumina is affected primarily by the surface acidity of alumina． Key words：alumina；BaO；La2O3；preparation method 一 2o 由于其特有的织构性能和表面性质而 影响；Masuda等㈣报道了制备方法对CeO ／BaO／ 广泛应用于催化燃烧．甲烷蒸汽重整．汽车尾气净 Alumina稳定性的影响．但有关不同制备方法中镧 化等领域【 。氧化铝作为三效催化剂常用载体，其 钡协同作用对氧化铝性能的影响还未见报道 本工 热稳定性、比表面积、孔容、孔径分布、表面酸性以 作用4种方法制备了镧钡共改性的氧化铝．考察了 及NO吸附能力在很大程度上影响催化剂的催化性 制备方法和助剂引入方式对氧化铝性能的影响 并 能 咽，因此提高 一 2o 的高温热稳定性和表面性 以改性氧化铝为载体制备了单Pd整体式催化剂． 能对提高催化剂的活性和使用寿命具有重要意 结果表明共沉淀法制备的氧化铝为载体的催化剂 义[51。研究表明，通过添加稀土、碱土元素和SiO 等 表现出对丙烷最好的催化活性。 可以提高氧