竹木层积塑化板的研制.pdfVIP

湖南林业科技 2008年第35卷第1期 赫产工业 竹木层积塑化板的研制 刘忠会，赵仁杰，宋作梅 (中南林业科技大学，湖南长沙 410004) 摘 要：以竹席、杨木单板、底层纸和水溶性酚醛树脂胶为原料，将竹席先行水煮、然后进行干燥、浸胶并再干燥，杨 木单板进行两次双面涂胶，底层纸则通过浸胶、干燥成胶膜纸，然后组合成以竹帘为芯层，杨木单板为内层，胶膜纸为 表层的板坯，采用“冷一热一冷”胶合工艺，压制成强度高，吸水厚度膨胀率小的竹木层积塑化板。 关键词：竹席；塑化；层积；胶合 中图分类号：TS 653．3 文献标识码：A 文章编号：1003—5710(2008)01一oo44-03 Research on plastic panel of laminated bamboo and wood LIU Zhonghui，ZHA0 Renj ie，SONG Zuomei (Central South University of Forestry＆Techndogy，Changsha 410004，China) Abstract：T panels are made with bamboo mats，poplar veneers，bottom paper and water—soluble PF，Firstly，steep bamboo mat in PF resin after braising and drying，then dry it again，spread glue on two sides of polar veneer twice，steep the bottom paper in glue and then dry． Using bamboo as core，polar veneer as cross band and paper as face，then press them together using“cold—hot—cold’’ process，we can get the plastic panel of laminated bamboo and wood．The intensity of the panel is higher and its thickness swell is low— er． Key words：bamboo mat；plasticization；laminated bamboo 当今诸多高性能的材料都属于复合材料。例如国外最 干燥箱，电子天平。 新的建筑模板是以高强度的铝合金板为表层材料，用工程塑 1．3 试验方法 料板为芯层材料复合而成，这种复合结构由于复合效应和合 为了得到强度较高，竹席，杨木单板与酚醛树脂充分塑 理地利用了各自材料的特性而具有优良的物理力学性能。 化的层积塑化板，选取使用的竹席层数，成型的热压时间，竹 为了提高建筑业当今广泛使用的竹(木)胶合板模板的性能， 席的浸胶时问，以及是否软化处理作为实验因素。每个因素 采用与木材层积塑料相类似的工艺方法，以竹席，杨木单板， 选取三个水平，其中软化处理时间选取两个水平，进行正交 底层纸和水溶性酚醛树脂胶为原料，压制成竹木层积塑化 试验。因素水平安排见表l。 板，用作普通竹(木)胶合板模板的贴面材料或代替三聚氰胺 表1 试验因素和水平 板 用于装饰，也为今后研制一种性能较高的新型建筑模 板创造条件。 1 试验材料及方法 1．1 试验材料 竹席采用“挑二压二”的方式手工编织，竹席的竹篾厚 1．4 试验过程 0．6 mm；杨木单板为旋切单板，厚1．4 mm；酚醛胶为2122型 (1)将需软化的竹席放在水浴锅中蒸煮l h，然后在干 酚醛胶，分子量小，固体含