preparation of dispersed particle gel (dpg) through a simple high speed shearing method制备分散粒子凝胶(dpg)通过一个简单的高速剪切的方法.pdfVIP

Molecules 2012, 17, 14484-14489; doi:10.3390/molecules171214484 OPEN ACCESS molecules ISSN 1420-3049 /journal/molecules Communication Preparation of Dispersed Particle Gel (DPG) through a Simple High Speed Shearing Method Caili Dai 1,*, Guang Zhao 1,*, Mingwei Zhao 1 and Qing You 2 1 State Key Laboratory of Heavy Oil Processing, China University of Petroleum, Qingdao 266580, Shandong, China; E-Mail: zhaomingwei@ 2 School of Earth and Space Sciences, Peking University, Beijing 100871, China; E-Mail: youqing_dandong@ * Authors to whom correspondence should be addressed; E-Mails: daicl306@163.com (C.D.); zhaoguang.sdau@163.com (G.Z.); Tel.: +86-532-8698-1183 (G.Z.); Fax: +86-532(G.Z.). Received: 9 October 2012; in revised form: 14 November 2012 / Accepted: 26 November 2012 / Published: 6 December 2012 Abstract: Dispersed particle gel (DPG) has been first successfully prepared using cross-linked gel systems through a simple high speed shearing method with the aid of a colloid mill at room temperature. The gel microstructure and particle size were investigated by scanning electron microscope (SEM), transmission electron microscope (TEM), and dynamic light scattering (DLS) measurements. The results clearly show that the prepared DPG particles have highly uniformly spherical structures with an average size of 2.5 μm. A possible mechanism for the formation of DPG has been put forward and discussed in details. The high speed shearing method is considered to be th