冷冲模材料与热处理（Die material and heat treatment） Cold stamping die, cold work parts, materials and heat treatment Mold type Common materials heat treatment Hardness (HRC) Die punch Blanking die The shape is simple and the blanking sheet thickness is less than 3mm T8A, T10A, 9Mn2V, Cr6WV, GCr15, 45# hi Quenching and tempering 58~62 58~62 The shape is complex and the blanking sheet thickness is 3mm. It requires high wear resistance CrWMn, 9SiCr, Cr12, Cr12MoV, Cr4W2MoV D2 Quenching and tempering 58~62 58~62 Bending die General bending die T8A, T10A Quenching and tempering 54~58 56~60 Requirements of high wear resistance, complex shape, production of large quantities of bending die CrWMn, Cr12, Cr12MoV, Cr12Mo1V1 Quenching and tempering 58~62 58~62 Hot bending die 5CrNiMo, 5CrMnMo H13, 3Cr2W8V Quenching and tempering 48~52 48~52 Drawing die General drawing die T8A, T10A, GCr15 Quenching and tempering 55~58 55~58 Requirements of high wear resistance, large batch production drawing die Cr12, Cr12MoV, YG8, YG15, D2 Cold worked die Cold stamping die in the fastener industry mainly complete the blanking, bending, drawing, upsetting, extrusion and other processes of metal or nonmetal materials, making all kinds of bolts, screws, nuts, gaskets, pins, rivets and so on. As the loading form and the mechanical properties of the material to be processed are different, the working conditions of various dies vary greatly, so the failure modes are different. In the above mold, the worst working conditions of the die are upsetting die and extrusion die, and then the minor plate blanking die. 2. cold working die failure Upsetting dies and extrusion dies are mainly used for the manufacture of bolts, nuts and shaped parts. It is used for metal bulk forming. The load of forming die is different according to the working shape, size, deformation and mechanical properties of the deformed material. In production due to deformation of metal in the mold cavity in the turbulent flow have serious fric