高碘酸钠氧化对棉纤维基吸附剂吸附性能影响 　　摘要：文章通过碱活化棉纤维，经环氧氯丙烷环氧化和高碘酸钠氧化制备双氧化棉纤维，先后接枝β-环糊精和端氨基超支化聚合物，制备了一种棉纤维基吸附剂。对制备的吸附剂进行了表征，并通过模拟废水吸附实验优化了吸附剂制备过程中高碘酸钠对棉纤维的氧化工艺。结果表明，当高碘酸钠浓度为12 g/L，50 ℃水浴氧化反应 3 h制备的吸附剂对Pb2+和刚果红的吸附容量达到最大值，最大吸附容量分别为65.7 mg/g和223.7 mg/g。 关键词：棉纤维；氧化；吸附剂；Pb2+；刚果红 中图分类号：TQ085 文献标志码：A Effect of Sodium Periodate Oxidation on Adsorption Properties of Cotton Fiber-based Adsorbent Abstract： In this paper， a kind of adsorbent was prepared by grafting β-cyclodextrin and amino-terminated hyperbranched polymer after the alkalization of cotton fiber through epoxy chloropropane epoxidation and sodium periodate oxidation. The prepared adsorbent was characterized. The oxidation technology for cotton fiber was optimized according to adsorption experiments with model wastewater. The result indicated that the cotton fiber-based adsorbent has best adsorption capacity to Pb2+ and Congo red when the cotton fibers were oxidized with 12 g/L sodium periodate at 50 ℃ for 3 h. The maximum adsorption capacity to Pb2+ and Congo red can reach 65.7 mg/g and 223.7 mg/g respectively. Key words： cotton fiber； oxidation； adsorbent； Pb2+； Congo red 纺织工业所产生的各种废水中含有大量重金属离子以及各种染料和染整助剂等，这些废液一旦处理不当就会对水体产生破坏，如总磷氮含量增高，使水体富营养化，并可随食物链进入植物体、动物体乃至人体，并在人体内蓄积，危害人们的身体健康。纤维素作为自然界最为丰富且价格低廉的可再生资源，具有多孔性、高比表面积、无污染、易生物降解等特性，同时纤维素大分子内含有许多亲水性的羟基基团，这些优势都为其用作吸附材料提供了良好的基础。目前，利用纤维素基吸附材料来吸附、分离、提取过渡金属离子和贵重金属离子，已逐渐成为国内外研究的热点。 但是，天然纤维素吸附容量小，选择性低，这是由于纤维素分子结构单一的羟基基团，以及分子链间和分子链内部广泛形成的氢键降低了其反应活性。为了使纤维素达到人们所预期的吸附功能，需要对纤维素进行改性，制备一系列纤维素基吸附材料。β-环糊精（β-CD）是由 7 个葡萄糖分子通过α-1，4-糖苷键形成的环状低聚糖，具有 1 个环外亲水、环内疏水且有一定尺寸的锥形筒状空腔。β-CD特殊的疏水性空腔可以包络尺寸大小适宜的有机物分子，并且其分子表面分布的众多化学反应性羟基对金属离子具有螯合作用。端氨基超支化聚合物（HBP-NH2）因其独特的准球形分子结构和丰富的伯胺基和亚氨基，表现出高溶解度、低黏度、高反应活性等许多线型聚合物所不具有的特殊性能，这些活性基团有助于螯合重金属离子，同时内部的孔隙也有助于吸附染料等有机污染物。 本文以棉纤维为载体，在已有的棉纤维经环氧化后接枝β-CD工艺的基础上，通过将环氧化后的碱化棉纤维进行双醛氧化，制得环氧化双醛氧化棉纤维，再先后接枝β-CD和HBP-NH2以制备新型棉纤维基吸附剂。探讨了双醛氧化工艺中氧化剂浓度、温度、时间对制备的吸附剂吸附性能的影响，并利用红外光谱和扫描电镜对吸附剂进行了表征。 1 实验部分 1.1 实验试剂与仪器 实验材料和试剂：棉纤维（市售），试剂有HBP-NH2（实验室自制）、NaIO4、环氧氯丙烷、