有机磷酸盐类成核剂的研究进展.docx

有机磷酸盐类成核剂的研究进展池圣贤乐道进徐祥兵龙林林( 湖北省化工研究设计院, 武汉, 430074)摘 要 介绍了聚丙烯成核剂中有机磷酸盐类成核剂的研究状况, 着重介绍了其在 PP 中的应用研究情况, 特别是与其他助剂的协同作用,并提出了我国有机磷酸盐类成核剂的发展建议。 关键词 聚丙烯 成核剂 有机磷酸盐类 性能 协同效应Resear ch and Development of the Or ganophosphate Nucleating Agents for Polypr opyleneChi Sheng- xianYue Dao- jinXu Xiang- bing Long Lin- lin(Hubei Research and Design Institute of Chemical Industry, Wuhan, 430074)Anstr act: The research and development of the organophosphate nucleating agents for polypropylenewere summarized in this paper. The research and application of the organophosphate nucleating agents, espe- cially its synergism with other plastic additives, in polypropylene were pointed out emphatically. And some suggestions for domestic derelopment of the organophosphate nucleating agents were put forward.Keywor ds: polypropylene; nucleating agent; organophosphate; property; synergism聚丙烯成核剂是一种用来改变聚丙烯( PP) 结晶行为, 从而改变其结晶形态, 最终改善其物理机 械性能、光学性能和热力学性能的功能性助剂。通 过在 PP 中添加少量的成核剂, 可以有效地改变 PP 的结晶形态, 实现 PP 刚性、韧性、热变形温度、 蠕变性能、透明性及制品表面光泽度等物理机械 性能与加工性能的改善, 从而提高制品的使用性 能, 拓宽应用范围。随着世界塑料工业的迅猛发展 和对成核剂认识的逐步深化, 近年来, 成核剂的研 究开发及其应用工作已受到普遍关注。然而值得 指出的是, 有关聚烯烃成核剂的研究开发或者应 用研究大都集中在二苯亚甲基山梨醇及其衍生物 这类成核剂上, 而对于某些性能更为优异的有机 磷酸盐类成核剂的研究则相对较少[1]。与其他有机 成核剂相比, 有机磷酸盐类成核剂能够显著提高聚合物的结晶速率, 降低雾度, 提高制品的透明性;特别是对材料热力学性能和机械加工性能更有显 著改善; 并且热稳定好, 在高温条件下, 不产生异味 和变色, 也不影响聚合物制品的其他性能, 从而大 大拓宽了聚合物制品的应用范围。笔者特就近年来 有机磷酸盐类成核剂的研究情况进行综述。1品种及其特点有机磷酸盐类成核剂主要包括有机磷酸酯和有机磷酸碱式金属盐及其复配物等, 最早是由日本 旭电化公司( ASAHI DENKA KOGYO) 开发应市的。 和山梨醇类成核剂相比, 有机磷酸盐类成核剂的品 种较少。根据产品开发年代的不同可划分为三代产 品。第一代产品问世于 20 世纪的 80 年代初, 产品 牌号为 ADK Stab NA- 10, 相对于山梨醇类成核剂 而言, 该产品不析出, 无异味, 而且成本低廉, 但成核效果一般,多用于 PP 增刚改性。第二代产品为收稿日期: 2005- 11- 1513第 1 期池圣贤, 等. 有机磷酸盐类成核剂的研究进展ADK Stab NA- 11, 该产品熔点高, 热稳定性突出,成核能力强, 其成核性能优于 NA- 10, 但分散性差, 容易导致制品表面出现白斑。第三代产品为 ADK Stab NA- 21, 该产品是由多种组分复配而成[2],与前两代产品相比, NA- 21 熔点较低, 分散性好, 成核效率更高, 使用效果也较好, 但价格比较昂贵。有 机磷酸盐类成核剂品种的具体化学名称、结构及 其特点如表 1 所示[2～4]。表 1 有机磷酸盐成核剂的品种及其特点Tab.1 Varieties and characteristics of organophosphate nucleators牌号化学名称结构 式熔点/℃特点OPONa双 ( 4 - 叔