混凝土断裂过程区考虑应力―应变全曲线损伤损伤模型.docVIP

混凝土断裂过程区考虑应力―应变全曲线损伤损伤模型 　　Concrete fracture process area consider stress-strain full curves of damage damage model 　　Liu fang 　　(guangdong guangdong road survey and design Co., LTD. Guangdong guangzhou 510635) 　　 　　 　　摘要：由于微裂缝不断形成和扩展，在混凝土结构宏观裂缝前缘存在一定范围断裂过程区。混凝土 曲线中，应力达到峰值之前损伤较少，但也有一定影响，考虑 全曲线损伤有一定的实际意义，基于虚拟裂缝模型，结合损伤力学，建立损伤模型，计算断裂过程区等效裂缝长度值 及其相应的临界损伤度 。 　　关键词:断裂过程区，损伤模型，损伤度，等效缝长。 　　Abstract: due to the constantly forming tiny cracks and expand, in the concrete structure crack front range, there are certain macro fracture process area. Concrete curve, the peak stress before less damage, but also have certain effects, considering all the curve is of certain practical significance damage, based on virtual crack model, combined with the damage mechanics, establish damage model, the calculation of fracture process area equivalent crack length value and corresponding critical degree Dl. 　　Keywords: fracture process area, damage model, degree, equivalent seam long 　　 　　 　　中图分类号：TU528 文献标识码：A 文章编号： 　　1引言 　　本文以初始缝长 的混凝土单轴拉伸构件为研究对象，考虑混凝土 全曲线损伤的影响，基于虚拟裂缝模型[1]，分析该情况下 形式的损伤演变方程和损伤模型，运用损伤力学理论推导断裂过程区[1[2]的等效裂缝长度 及其相应的临界损伤度 的计算公式。 　　2基于虚拟裂缝的损伤模型 　　损伤因子 为： （1） 　　直杆受到沿杆轴线方向外力F拉伸时，则有： （2） 　　式中: 为横截面面积； 为名义应力； 为有效面积； 称为净应力或有效应力，即有效面积上作用的应力。由式（1）和（2）式可推出: 　　损伤变量D为：（3） 　　显然， 对应于无损状态； 对应于完全损伤(破坏)状态； 对应于不同程度的损伤状态。原生缺陷或界面裂隙发展成微裂纹以至微裂纹区和宏观裂缝，则可以看成是损伤积累的结果。 　　损伤模型考虑混凝土 全曲线损伤的影响因素， 曲线，如图1；其对应的损伤演变曲线 曲线，如图2；其对应的损伤模型，如图3。 　　 　　图1曲线 图2损伤演变曲线图 3基于虚拟裂缝的损伤模型 　　损伤模型考虑 全曲线损伤，更进一步分析实际问题，也更真实。折线OED为无损伤的混凝土 曲线，实际的混凝土 全曲线都是有损伤的，为折线OAB；其中区域OEA是混凝土 曲线上升段损伤形成的损伤区域，区域ACDB是混凝土 曲线下降段损伤形成的损伤区域，将区域OAMGE的损伤转移到区域MNB，造成区域MNB的损伤，即 ；B点完全损伤，故进行损伤折算后，区域GNBD完全损伤。此时，断裂过程区的等效裂缝长度为： 。 　　 （4） 　　（5） 　　AE段长度对应着损伤度 ，在损伤度为 时，有大小为 的应变；DB段长度对应损伤度为1，即完全损伤，此时应变为 ，即极限应变。 　　 ， ， ， 。 　　由图3知， 可表示为：（6） 　　 （7） 　　 （8） 　　（9） 　　又由图3知：（10） 　　 （11） 　　（12） 　　（13） 　　将式（12）和式（14）代入式（10）得： 　　（14） 　　断裂过程区的等效裂缝长度 所对应的临界损伤度 ： 　　（15） 　　实验算例中：如果已知初始损伤 、峰值损伤 、峰值应变 、极限应变 ，将它们代入到式（14），便可以计算出 ，然后再代入式（5），计算断裂过程区的等效裂