色织高支高密织物浆纱工艺的探讨.docVIP

色织高支高密织物浆纱工艺的探讨 　　摘要：高支高密品种因其纱支细、织物密度大等特点，织机经停高、织造效率低，特别是色织高支高密经过染色后，其单纱强力、伸长、毛羽等指标比原纱指标更差，因此生产难度更大。本文重点从纱线的质量要求、高支纱浆料配方、浆纱工艺等方面，讲述了高支高密织物上浆的工艺难点和技术措施，有效地降低了织机经停，提高了色织高支高密品种织造效率。 　　关键词：高支高密织物；浆纱；浆纱工艺 　　中图分类号：TS105.213 文献标志码：B 　　An Approach to the Sizing Process for High-count High-density Yarn-dyed Fabric 　　Abstract： Due to fine yarn count and high fabric density， the production of high-count high-density fabric is often accompanied with high warp breakage rate and low weaving efficiency， especially after the fabric being dyed， the single-end strength， elongation and hairiness indicators of the yarn are poorer than those of the original yarn， which make the fabric more difficult to produce. The paper introduced the difficulties and related technical measures in sizing of high-count high-density fabric by discussing the quality requirements on yarn， size formula for high-count yarn and the sizing process， which can help reduce machine stop due to warp breakage and improve weaving efficiency of high-count high-density yarn-dyed fabric. 　　Key words： high-count high-density fabric； sizing； sizing process 　　高支高密织物具有手感细腻柔软、光洁如绸等特点，是纺织行业进一步深加工、提高产品附加值的一个发展方向。高支高密品种因其纱支细、织物密度大等特点，织机经停高、织造效率低，特别是色织高支高密经过染色后，其单纱强力、伸长、毛羽等指标比原纱指标更差，因此生产难度更大。本文通过对高支高密品种浆料配方、浆纱工艺的优化和采取的技术措施进行了探讨。 　　1 纱线是基础 　　高支高密织物一般指纱支≥60S、经密在185根/英寸以上品种。高质量的纱线是织造好高支高密织物的基础，特别是纱线的强力、棉结、纱疵方面都有严格的指标要求。 　　1.1 原纱与染色后纱线指标对比 　　通过实验数据对比（表1），发现经纱染色后其单纱强力、断裂伸长率以及耐磨性均有所下降，3 mm毛羽指数则有所增加，因此色织高支高密品种对浆纱的要求更高。 　　2 浆纱是关键 　　高支高密品种经纱根数多、单纱强力低、伸长差，在织造过程中与综丝、停经片、钢筘之间的摩擦剧烈，如果上浆不良会造成经纱在综丝、停经片、钢筘断头增加，影响织机效率。因此，浆纱是关键。 　　2.1 浆纱工艺配方 　　浆料配方是保证浆纱质量的基础，配方的合理与否会直接影响浆纱指标的提升。高支高密织物的上浆以“渗透、增强、保伸、耐磨”为主。 　　在原高支纱配方的基础上引进了固体丙烯AG与原来的液体丙烯进行比较（表 2），液体丙烯酸类浆料含固量一般为20% ～ 25%，固体丙烯酸类浆料与其相比具有运输成本低、搬运轻便、储存空间小等优点，调浆时能减轻调浆工的劳动强度。 　　从表 2 可以看出：随着固体丙烯浆料AG的增加，液体丙烯浆料用量减少。 　　2.2 粘度稳定性对比 　　粘度是浆液质量的一个重要指标，色织品种浆纱时因为换批、换浆较多，因此要求浆液粘度稳定性要好，对 3 种配方的调浆桶粘度稳定性进行测试（表 3、图1）。 　　从表 2、表 3、图 1 可以看出，随着固体丙烯浆料AG的增加，浆液粘度逐渐降低，这对经纱根数多的高支高密品种来说，更有利于浆液对纱线的渗透。试验配方2