自酸蚀黏结剂结合流动复合体窝沟封闭中临床疗效观察.docVIP

自酸蚀黏结剂结合流动复合体窝沟封闭中临床疗效观察 　　摘要：目的应用自酸蚀粘接剂结合Beautifi流动复合体对年轻恒磨牙进行窝沟封闭术，观察封闭材料的3年随访保留率和龋降低率。方法选择200例7~12岁儿童已完全萌出第一恒磨牙800颗采用自身半口对照方法，随机选择一侧为实验组，采用自酸蚀黏结系统进行窝沟封闭；另一侧为对照组，酸蚀后用窝沟封闭剂进行窝沟封闭，并随访观察3年。结果术后3年复查时实验组窝沟封闭剂保留率高于对照组，龋病发病率低于对照组，除第１年龋病发病率外其余数据均有统计学差异（P0.05）。结论自酸蚀黏结剂结合流动复合体进行窝沟封闭，可提高材料保留率，有效预防年轻恒牙窝沟龋的发生。 　　关键词：自酸蚀黏结剂；流动复合体；窝沟封闭 　　The Clinical Effect Observation of Self-etching Adhesive Bonding with Flow Resin Used in Pit and Fissure Sealants 　　HAN Xia 　　(Department of Stomatology, The Second Hospital Affiliated to Zhejiang Chinese Medical College,Hangzhou 310005,Zhejiang,China) 　　Abstract：ObjectiveTo observe the 3-year follow-up of pit and fissure sealant retention and caries reduction rate when using self-etching adhesive bonding with Beautifi flow resin. Methods 800 permanent molars in 200 patients aged from 7 to 12 years treated with self-etching adhesive and Beautifi flow resin. The opposite permanent teeth were treated with traditional methods as the controls. They were followed up for 3 years. Results1,2,3 years after application of the treatment, the remain rate of self-etching adhesive bonding with Beautifi flow resin were higher than the total-etching adhesive. And the rate of caries were lower. They have significant difference(P0.05). ConclusionSelf-etching adhesive bonding with flow resin can prevent caries in permanent molar effectively. 　　Key words：Self-etching adhesive; Flow resin; Pit and fissure sealants 　　目前，我国儿童的龋病发生率仍很高，据调查，6~12岁儿童龋病发生率达40%~50%，其中窝沟龋病发生率占80%[1]。窝沟封闭剂涂布窝沟是预防窝沟龋发生的一种有效方法[2]。自酸蚀黏接系统因操作简便而提高了患者的配合度。本研究希望推广一种更简便快捷有效的窝沟封闭方法，研究方法如下。 　　1资料与方法 　　1.1一般资料2010年3月~2011年3月在本院口腔门诊选择7～12岁儿童200例；其中男108例，女92例；纳入标准：第一恒磨牙牙冠完全萌出 ，牙合面无修复体，窝沟较深，无氟牙症，非四环素牙，无釉质发育不全，能配合者。 　　1.2材料Beautifil flow(商品名为卓美)流动聚合体及相配套的 FL2 Bond自酸蚀含氟粘接剂(Shofu公司,日本)，35％磷酸酸蚀剂（贺利氏公司，北京），光固化型窝沟封闭剂(3M公司，美国)，光固化机（登士柏公司，美国）。 　　1.3方法自酸蚀组(实验组)：将第一恒磨牙牙面彻底清洁隔湿干燥后，用小棉球蘸有自酸蚀黏结剂涂布在需要封闭的牙面上，以气枪轻吹使其成一层薄膜，再将流动复合体涂布在窝沟处，以可见光固化每个牙面40s。 　　磷酸酸蚀组(对照组)：将第一恒磨牙牙面彻底清洁隔湿干燥后，用35%磷酸酸蚀牙面后彻底冲洗，吹干牙面至白垩色，