锂离子电池负极材料钛酸锂的制备改性及其应用-应用化学专业论文.docxVIP

exhibited a initial charge capacity of 994.6 mAh and a initial discharge capacity of 778.6mAh with a coulombic efficiency of 78.3%; At 0.2C,a capacity of 858mAh was released, but the capacity had been decayed to 815,738,660.66mAh when discharged at 0.5C, 1C and 2C respectively. So the capacity decayed significantly as the discharge rate increased. The capacity retention of designed cell (Vs room temperature) was 73.5%, 54.8% and 30% at 0℃，-10℃ and -20℃ respectively. But the expansion was observed at 60℃which may be brought by the excessive side reactions between LTO and electrolyte at high temperature. LTO/LiFePO4 cell exhibited excellent cycle stability at 1 C with no obvious capacity loss after 800 cycles. KEY WORDS：lithium titanate, lithium-ion battery, anode material, dope 目 录 目 录4 第一章 绪论1 1.1 选题背景1 1.2 锂离子电池概述1 1.2.1 锂离子电池发展概况1 1.2.2 锂离子电池组成和工作原理2 1.2.3 锂离子电池优缺点4 1.3 锂离子电池负极材料研究进展5 1.3.1 锂离子电池负极材料的发展历史5 1.3.2 锂离子电池负极材料的要求5 1.3.3 锂离子电池负极材料的分类6 1.3.3.1 碳基材料6 1.3.3.2 硅基材料8 1.3.3.3 锡基材料8 1.3.3.4 过渡金属氮化物材料9 1.3.3.5 其他材料10 1.3.4 锂离子电池负极材料钛酸锂研究进展10 1.3.4.1 Li4Ti5O12 结构特性与嵌锂机制 10 1.3.4.2 Li4Ti5O12 制备方法 11 1.3.4.2.1 传统制备方法11 1.3.4.2.2 特殊制备方法12 1.3.4.3 Li4Ti5O12 掺杂改性研究 13 1.3.4.4 表面修饰改性研究13 1.3.4.5 钛酸锂作为负极材料的应用15 1.3.4.6 钛酸锂作为包覆材料的应用16 1.3.4.7 钛酸锂材料总结16 1.4 选题依据17 1.5 本论文的主要研究内容17 第二章 实验部分18 2.1 实验原料18 2.2 实验仪器19 2.3 电极材料的合成与扣式电池的装配19 2.3.1 电极材料的合成19 2.3.2 扣式电池装配20 2.4 材料表征及电化学性能测试21 SEM（扫描电子显微镜）观察 21 XRD（粉末X射线衍射）分析 21 EIS(交流阻抗谱)测试 21 2.4.4 恒电流充放电测试21 第三章 高温固相法合成钛酸锂及其电化学性能研究23 3.1 锂源对材料性能的影响23 3.2 焙烧温度对材料性能的影响27 3.3 焙烧时间对材料性能的影响32 3.4 焙烧气氛对材料性能的影响36 3.5 本章小结41 第四章 钛酸锂的掺杂改性研究42 4.1 引言42 4.2 16d锂位掺杂 45 4.2.1 实验流程45 4.2.2 结果与讨论45 4.316d钛位掺杂 49 4.3.1 实验流程49 4.3.2 结果与讨论50 4.432e氧位掺杂 57 4.4.1 实验流程57 4.4.2 结果与讨论57 4.5 本章小结61 第五章 以钛酸锂为负极的全电池设计62 5.1 引言62 5.2 锂离子电池设计规范62 5.3 设计流程63 5.3.1 正负极材料选择63 5.3.2 设计容量确定63 5.3.3 计算电池正、负极活性