间戊二烯石油树脂改性聚合工艺的研究.docxVIP

第41卷第8期 2012年8月Vol.41 No.8Aug. 2012应 第41卷第8期 2012年8月 Vol.41 No.8 Aug. 2012 Applied Chemical Industry 间戊二烯石油树脂改性聚合工艺的研究 张贺东 (大庆华科股份有限公司，黑龙江大庆 163714) 摘 要：采用Cs分离装置得到的单烯烃馏分对间戊二烯石油树脂进行改性，研究了单烯烃加入量、溶剂比和催化 剂加入量等工艺参数对树脂性能的影响。结果表明，路标漆用间戊二烯石油树脂的最佳聚合工艺条件为：单烯烃 加入量为33.0%,溶剂比为0.6以及催化剂的加入量为0.85%。 关键词：间戊二烯石油树脂；单烯烃；聚合工艺 中图分类号：TQ 326.82 文献标识码：A 文章编号：1671-3206(2012)08-1399- 03 Study on the polymerization technique of monoolefin fraction modified piperylene-based petroleum resin ZHANG He-dong (Daqing Huake Co.,Ltd.,Daqing 163714,China) Abstract: A piperylene-based petroleum resin was modified by the monoolefin fraction from Cs separation unit. The effects of process parameters for the amount of monoolefin,catalyst and ratio of solvent on resin performance were studied. The results showed that traffic paint with the optimum of piperylene petroleum resin polymerization conditions the amount of monoolefin was 33.0%,ratio of solvent was 0.6 and catalyst amount was 0.85%. Key words:piperylene petroleum resin; monoolefin; polymerization technique 石油树脂这一名称，随着化学工业的发展其含 义有所不同，最早把从石油为原料制成的似树木分 泌物——树脂状物质称之为石油树脂，按现代观点， 一般认为石油树脂是以裂解制乙烯副产的Cs、C,馏 分合成的一种低分子量的热塑性烃类树脂。按其合 成原料的不同，主要分为脂肪族树脂、脂环族树脂、 芳香族树脂、共聚改性石油树脂以及氢化树脂等。 近年来随着我国 Cs、C,馏分数量逐年增加，2010年 已经达到150万 t/a 以上，如何利用此部分资源进 一步加工生产，提高企业的经济效益已经成为一个 重要的课题，经过研究利用此部分资源采取多塔精 馏分离后生产石油树脂是其重要的使用途径。 目前，随着各行业对石油树脂各项指标需求的 提高，为此对原有石油树脂产品质量的提高或对性 能的改进以满足市场需求的问题，已日渐突出。作 为路标漆行业的主要原料间戊二烯石油树脂的市场 需求量逐年上升，如何解决间戊二烯树脂在路标漆 行业应用过程中由于流动性不好而只能在低档路标 漆中应用的难题，通过实验在间戊二烯树脂聚合原 料中按一定比例混配单烯烃进行聚合反应，改进树 脂的性能，以满足间戊二烯树脂在高端路标漆行业 中的应用，同时也为化学改性石油树脂领域提供了 重要依据。 1 实验部分 1.1 试剂与仪器 粗间戊二烯、溶剂、Cs 单烯烃组成见表1;三氯 化铝、氢氧化钠均为工业品。 BL-1L 型夹套玻璃反应釜；BL-2L 夹套玻璃水 洗釜；JSOB 型恒温水浴锅；安捷伦6890N 型气相色 收稿日期：2012-04-26 修改稿日期：2012-05-14 作者简介：张贺东(1962-),男，黑龙江大庆人，大庆华科股份有限公司工程师，主要从事石油烃类裂解副产物的综合利 用以及树脂改性开发工作。电话：0459-6562622,E-mail:zhz628402@ 1400 应用化工 第41卷 谱仪；M21043 型真空泵；SYD-2806 沥青软化点测定 仪；NDJ-1D 旋转粘度计。 表1 主要原料组成 T