微胶囊化红磷无卤阻燃HDPE聚乙烯的研究.pdfVIP

微胶囊化红磷无卤阻燃 HDPE聚乙烯的研究 微胶囊化红磷无卤阻燃 HDPE 聚乙烯的研究 摘 要 聚乙烯作为塑料产品，广泛的用于制造电缆，管道，薄膜。与人们日常生活密 不可分。但是由于其氧指数低燃烧时发热量大，产生浓烟和有毒气体，造成对环境 的污染和危害。 本论文中，三聚氰胺－甲醛树脂包覆红磷微胶囊阻燃剂制取，作为阻燃剂添加 入高密度聚乙烯，同时对不同添加量进行对比和分析，通过对试样的阻燃和力学性 能的测试，可以发现，随着微胶囊红磷的添加量的增加，高密度聚乙烯的阻燃性能 呈上升趋势，但其力学性能，可加工性能呈下降趋势。 关键词：高密度聚乙烯 阻燃剂 性能 - 3 - 微胶囊化红磷无卤阻燃 HDPE聚乙烯的研究 Abstract HDPE, as one of the most productive resins, has been widely used in many industries and area. On account of the low oxygen index (0I) value, HDPE is prone to burn and gives off a lot of heat and toxic gas ,which is harmful to environment. In this paper , RP coated by melamine formaldehyde resin as non –halogen flame-retardant additives for HDPE was studied .As the same time , analyze to the different sample and then compare to them ,though Mechanical and flame-retardant property of adding to HDPE investigated respectively , as the adding increase ,as the flame-retardant property increased , and the mechanical declined . Keywords:polyethene flame-retardant properties - 4 - 微胶囊化红磷无卤阻燃 HDPE聚乙烯的研究 第一章………… 前言 6 1、研究背景及意义 6 1.1 选题背景： 6 1.2 研究意义 9 2.文献综述 10 2.1 塑料基体聚合物的燃烧过程和机制10 2.2 理想阻燃剂应满足条件 11 2.3.塑料基体聚合物的阻燃机制11 2.4 磷系阻燃剂的发展近况 16 第二章…………实验部分 17