高炉含锌粉尘中铁资源的富集回收研究.pdfVIP

高炉含锌粉尘中铁资源的富集回收研究 邢相栋，张建良，王振阳，刘兴乐，焦克新，任山 (北京科技大学冶金与生态工程学院北京100083) 摘要：以转底炉为基础，采用高温焙烧工艺对济钢高炉含锌粉尘脱锌富集铁进行实验室研究，考察了还原 温度、还原时间及配煤量对含锌粉尘脱锌率、金属化率的影响。实验结果表明最佳工艺参数为：还原温度 1350℃，还原时间30min，配煤量4％。在此条件下的脱锌率和金属化率分别高达99．75％和99．46％。 关麓词：含锌粉尘；磁选；脱锌率；金属化率 at onEnrichmentofFefromZincDustBlastFurnace Study Liu JiaoKe--xinRenShah XingXiang--dongZhangJian--liangWangZhenyangXingle 0 and 0fScienceand (SchoolfMetallurgicalEcologicalEngineering，UniversityTechnologyBcijl．g，Beijing 100083，China) ofFefromdustatblastfurnace hearthfurnaceWasstudiedin Abstract：Enrichmentzinc byrotary effectsof theamountof coalOil laboratory．Thereducingtemperature，reducingtime，and blending andmetallization arc was degree degree parameters de—zincing investigated．Theoptimalprocess asfollows：the is timeis the 1350℃，the 30min，and reducingtemperature reducing blending coalis4％．Underthis andmetallizationare condition，the pulverized de—zincingdegree degreeup t099．75％and 99．46％．respectively． ofmetallization Keywords：zincdust；magneticseparation；de-zincingdegree；degree 通常条件下，钢铁企业中产生的粉尘收集后一般作为烧结的原料来生产烧结矿，在钢铁 企业内部循环利用。由于这些粉尘粒度细，比表面积大，表面光滑，加湿比较困难并且含有 锌、铅、钾和钠等元素。烧结配入这些粉尘，一方面会降低烧结料层的透气性，影响烧结生 产的技术经济指标；另一方面由于某些粉尘(例如：高炉布袋除尘灰、转炉除尘灰、电炉除