烯丙基聚醚系超塑化剂合成参数研究 王晓丰 王子明 李庆蕾 （北京工业大学材料科学与工程学院，北京100022） 摘要 本文概括了一种以烯丙基聚乙二醇为原料的烯丙基聚醚系超塑化剂的合成研究。研究中采用自行设计的聚 合工艺，运用活性调节剂调节聚合速率，通过正交试验得到了较为理想的反应参数。研究解决了现有技 术存在的一系列问题。例如：聚合速率较慢，产品不稳定，应用性能不佳等。并且此技术可以应用于工 业化生产。 关键词 聚醚基超塑化剂 烯丙基聚乙二醇 正交试验 一步法 中图分类号：TU528.0 Study on synthesis parameters of polyether-based superplasticizer WANG Xiaofeng WANG Ziming LI Qinglei （Materials Science and Engineering Institute, Beijing University of Technology, Beijing, 100022 ） Abstract A research about polyether-based superplasticizer which used Allyl-PEG as raw materials was reviewed. This research adopted the technology which was designed on our own, increased the polymerization rate by some activity regulators, and gained series of perfect polymerization parameters by orthogonal tests. This research solved serials of problems in exiting technology. For example: the lowness of polymerization rates, the instability of products, the poor performance of application and so on. Besides this technology can be applied in industrial production. Key Words Polyether-based superplasticizer Allyl-PEG Orthogonal test One-step synthesis 0 前言 势在于：原材料国产化，质量稳定，价格低廉， 聚醚基超塑化剂在国内通常被称为聚羧酸 原料的封端基团中包含了不饱和双键，超塑化剂 系高效减水剂，是国内外公认的第三代减水剂 可通过一步法直接聚合。但原料的结构特点也使 [1] 。按照其主要结构可以被具体分为聚酯基超塑 得产品在性能上存在一些问题，如聚合速率慢， 化剂和烯丙基聚醚系超塑化剂。从目前国内研究 产品转化率不高，产品质低温储存时底部出现析 状况来看，大量工作都是以甲氧基聚乙二醇为原 晶现象，低掺量下产品保留性能差，适应性不佳， 料的聚酯基超塑化剂的制备研究，此种大单体作 很难实现工业生产等。本研究针对以上问题，自 为合成原料通常需要酯化和聚合两步工艺。尽管 行设计聚