浅析1215易切削钢铸坯修磨率的控制.pdfVIP

浅析1215 易切削钢铸坯修磨率的控制 ·1 · 浅析 1215 易切削钢铸坯修磨率的控制 张进红 李拥军 王秋坤 王建林 豆红卫 霍志斌 （邢台钢铁有限责任公司炼钢厂, 邢台 054027 ） 摘 要 本文重点就生产过程由脱氧不良造成的铸坯气泡，对某钢厂 1215 易切削钢各工序自由氧含量控制情况进 行了分析， 找出了造成该钢厂易切削钢铸坯气泡的主要因素，出钢氧含量控制不稳、转炉出钢下渣直接影响到铸 坯修磨情况。修磨率高的浇次平均上机氧含量为 38.9ppm，中间包平均氧含量比修磨率低的浇次高3.4ppm 。 关键词 铸坯气泡 易切削钢 修磨率 脱氧不良 Control the Slab Repair Grinding Rate of 1215 Free Cutting Steel Zhang Jinhong Li Yongjun Wang Qiukun Wang Jianlin Dou Hongwei Huo Zhibin (The Steelworks of Xingtai Iron Steel Corp., Ltd., Xingtai, 054027) Abstract This article focuses on the slab air bubbles caused by deoxy poor of production process, Through the analyse to the free oxygen content control of each process about 1215 cutting steel in a steel, the main factors causing the cutting steel slab bubbles were found out.the tapping oxygen content control unstable and tapping slag directly affect the slab repair grinding. High repair grinding rate poured times the average oxygen content is 38.9ppm after the end of LF, the tundish average oxygen content higher 3.4ppm than grinding low pouring times. Key words slab bubbles, free cutting steel, repair grinding rate, poor deoxy 1 概述 [1] 易切削钢作为世界三大难以连铸的钢种之一 ，由于钢种本身高氧含量、高硫含量的特点，大大降低了 钢水表面张力，使钢渣分离困难，造成钢渣混卷，形成大量表面及皮下缺陷[2, 3]，铸坯表面气泡如图 1 所示。 铸坯修磨成本高是大多数生产该钢种的钢铁企业面临的最大的问题。根据炼钢理论及前人的经验[4]，连铸过 程产生气泡（包括针孔）的主要原因有 3 类——脱氧不良、外来气体（空气、保护性气体）、水蒸气（来自 潮湿的添加料和耐火材料等）。本文结合某钢厂现场生产条件，重点就脱氧不良造成的铸坯气泡，研究了各 工序自由氧含量的控制与铸坯气泡的关系。 2 生产流程 某钢厂 1215 易切削钢生产流程为：混铁炉→50t 顶底复吹转炉→LF 精炼炉→连铸。连铸机为 4 机 4 流 2 ，工作拉速 1.8~2.0m/min，铸机具有结晶 渐