回火热处理参数对M2高速钢显微组织之影响-中国鑛冶工程学会互动式.PDF

回火熱處理參數對M2高速鋼顯微組織之 影響 The Effect of Tempering Heat Treatment on the Microstructure of M2 High-Speed Steel 1 1 2 3 4 Y.L. Peng, T.Y. Lin, S.Y. Huang, Y.T. Pan, D.Y. Lin AISI M2 This study focu sed on the microstructural change of AISI M2 high speed steel after different tempering treatments with 9 heat treatment parameters. This research attempted to quantify the volume fraction of retained austenite and carbide to check the change of microstructure FE-SEM XRD right after each tempering condition . We analyzed the microstructure and phase using FE-SEM and XRD. Results showed that the carbide content increased gradually with the increasing tempering temperature. It reached the highest 600 value, 9.08% when it was tempered at 600for 3 times. 9.08% The retained austenite decreased when tempered at a higher temperature. The retained austenite could not be eliminated 200 400 efficiently at 200 and 400; the amount of retained 24.73% 20.24% austenite was 24.73% and 20.24%, respectively. When it 600 was tempered at 600, the retained austenite content was 10.17% reduced to 10.17%. After the 3rd tempering treatment at 5% SEM 600, the amount of retained austenite was reduced to 5% XRD or less. The analysis of SEM and XRD showed a similar result. 關鍵字： Key words: h i gh sp e ed st e el , t emp er in g , r et ain ed austenite, carbide 壹、前　言 2010 1,098 1 4 2 3 1