冻干法保存脱细胞组织工程血管支架实验探究.doc

冻干法保存脱细胞组织工程血管支架实验探究[摘要]目的:探讨冷冻干燥技术长期保存脱细胞组织工程血管支架材料的可行性。方法:将制备的脱细胞组织工程血管支架预冷后置入-70℃、6.67×10-4kPa的冷冻干燥机内6 h作冷冻干燥处理。通过对冷冻干燥处理前后脱细胞血管支架材料的组织,超微结构观察、生物力学评估、细胞毒性测定以及动物体内的组织相容性检测,研究冷冻干燥处理对脱细胞血管支架材料生物相容性和生物力学特性的影响。结果:冷冻干燥处理对于脱细胞血管材料的生物力学及生物化学特性没有明显影响,处理后的材料依然具有良好的体内、外生物相容性。结论:冷冻干燥处理作为脱细胞组织工程血管支架材料的长期储存方法是可行的。 [关键词]组织工程血管;脱细胞组织工程血管支架;冷冻干燥 [中图分类号]Q813.1[文献标识码]A[文章编号]1008-6455(2010)02-0218-04 Conservation of the tissue-engineered acellular vascular scaffold with freezing and drying technique LIU Bin1, ZHANG Man-jing2, XIA Wei1, LU Kai-hua1,GUO Shu-zhong1 (Department of Plastic Surgery, Xijing Hospital,the Fourth Military Medical University,Xi′an 710032, Shaanxi,China 2.Department of Platic Surgery,the Second Affiliated Hospital of Kunming Medical College) Abstract: ObjectiveTo investigate the feasibility of a freeze-drying technique preservation protocol on the acellular vascular scaffold.MethodsAcellular vascular scaffolds were treated by freezing and drying technique at -70℃(6.67×10-4kPa) for 6h,then appraised the scaffolds by histological and ultrastructural observation and evaluated its biocompatibility and biomechanics.ResultsIt was shown that the main performance indexes of the freeze-drying treated acellular scaffolds changed unremarkably in compared with the untreated ones.ConclusionFreeze-drying technique can be a good preservation protocol for tissue-engineered acellular vascular scaffold. Key words: tissue engineering blood vessels; tissue engineered acellular vascular scaffold; freeze drying 随着科学技术的发展,组织工程学的兴起为从根本上解决血管移植物替代这一问题带来了新的曙光。组织工程血管是组织工程学领域的产物之一,是一种新的有望彻底解决小口径人工血管移植问题的方法。脱细胞血管基质因其具有取材方便、低免疫源性、机械性能良好等优良特性,在血管组织工程研究领域中得到了越来越广泛的应用[1-2], 成为该领域支架材料研究方面的一个热点。通过前期的系列试验研究,我们初步摸索出一种脱细胞血管支架快速制备、消毒及结构疏松化的方法。然而脱细胞血管材料制备后如何长期保存又是一个需要面临和解决的问题,因此我们希望找到一种简单可行的储存技术来长期保存制备的脱细胞血管支架以达到临床和科研上 “随用随取”的目的。 在本实验研究中我们使用冷冻干燥技术处理制备的脱细胞血管支架,通过对处理后的支架材料进行组织,超微结构观察、生物力学评估、细胞毒性测定以及动物体内的组织相容性检测,研究冷冻干燥处理对脱细胞血管支架材料生物相容性和生物力学特性的影响,从而进一步评估冷冻干燥技术作为该材料长期储存方法的可行性。